采用微弧氧化技术在钛合金表面制备了羟基磷灰石(HA)陶瓷膜.研究了电解液中乙酸钙、乙二胺四乙酸二钠(EDTA-2Na)质量浓度对膜层Ca、P含量和二者原子比的影响.随电解液中乙酸钙质量浓度增大,膜层表面孔隙率基本不变,膜层Ca含量增大,P含量减少,钙磷原子比增大,随电解液中EDTA-2Na质量浓度增大,膜层表面孔隙率先增后减,膜层中Ca含量明显增大,P含量略微增大,钙磷原子比明显增大.电解液的最佳组成为:K2HPO4·3H2O 6.8 g/L,Ca(CH3COO)2 26.5 g/L,EDTA-2Na 20 g/L.此时陶瓷膜层表面孔隙率高达11.10％,钙磷原子比为1.65,十分接近HA的钙磷原子比(1.67).
参考文献
| [1] | Li LH;Kong YM;Kim HW;Kim YW;Kim HE;Heo SJ;Koak JY .Improved biological performance of Ti implants due to surface modification by micro-arc oxidation.[J].Biomaterials,2004(14):2867-2875. |
| [2] | 屠振密;李宁;朱永明.钛及钛合金表面处理技术和应用[M].北京:国防工业出版社,2010:133-166. |
| [3] | 黄岳山,赵修华,吴源青.微弧氧化改性二氧化钛生物活性膜的研究进展[J].医疗卫生装备,2004(04):22-23. |
| [4] | Cheng, S.;Wei, D.;Zhou, Y. .Structure of microarc oxidized coatings containing Si, Ca and Na on titanium and deposition of cefazolin sodium/chitosan composite film[J].Surface & Coatings Technology,2011(13/14):3798-3804. |
| [5] | Mitsuo Niinomi .Recent research and development in titanium alloys for biomedical applications and healthcare goods[J].Science and technology of advanced materials,2003(5):445-454. |
| [6] | 王凤彪,狄士春.医用钛合金微弧氧化膜的制备及其生物相容性研究[J].电镀与涂饰,2011(06):25-28. |
| [7] | 杨瑞博 .钛合金表面微弧氧化生物活性涂层研究[D].长安大学,2012. |
| [8] | 赵睛,马刚,王帅星,邵志松,朱文辉.TC4钛合金微弧氧化因素对生物陶瓷膜中Ca，P相对含量的影响[J].材料保护,2012(01):42-44,55. |
| [9] | Rhee SH;Tanaka J .Effect of citric acid on the nucleation of hydroxyapatite in a simulated body fluid.[J].Biomaterials,1999(22):2155-2160. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%