使用叔丁醇(TBA)基凝胶-注模法制备莫来石多孔陶瓷材料,研究了不同干燥温度下坯体的失重、收缩以及最终的烧结.发现在较高的干燥温度下,坯体的失重较快,基本没有收缩,而在室温下干燥的坯体,失重较慢,具有较大的收缩.在高温下干燥的坯体,表层和内部水分的迁移速度不一,导致内部出现应力的不均匀,使得烧结后的材料出现较多的破碎.因此,使用叔丁醇基凝胶-注模法制备的多孔陶瓷材料坯体,初始低温干燥,后期高温干燥,可以得到长期保存并且烧结成功率较高的多孔陶瓷材料.
参考文献
| [1] | Jia-Min Wu;Xiao-Yan Zhang;Jin-Long Yang.Novel porous Si_3N_4 ceramics prepared by aqueous gelcasting using Si_3N_4 poly-hollow microspheres as pore-forming agent[J].Journal of the European Ceramic Society,20145(5):1089-1096. |
| [2] | R. Vasudevan;T. Karthik;S. Ganesan.Effect of microwave sintering on the structural and densification behavior of sol-gel derived zirconia toughened alumina (ZTA) nanocomposites[J].CERAMICS INTERNATIONAL,20133(3):3195-3204. |
| [3] | Wei Xiao;Chang Miao;Xianqing Yin;Yancheng Zheng;Minglei Tian;Hao Li;Ping Mei.Effect of urea as pore-forming agent on properties of poly(vinylidene fluoride-co-hexafluoropropylene)-based gel polymer electrolyte[J].Journal of Power Sources,2014Apr.15(Apr.15):14-20. |
| [4] | 王小锋;王日初;彭超群;王志勇.凝胶注模坯体的液体干燥[J].中国有色金属学报,2013(12):3374-3380. |
| [5] | 厉彦刚;王志义.不同干燥方式对凝胶注模成形陶瓷坯体干燥过程的影响[J].山东陶瓷,2011(6):26-28. |
| [6] | 刘飞;鲁中良;李振发;庞师坤;姜博;李涤尘.凝胶注模成型氧化铝基陶瓷坯体的冷冻干燥缺陷控制[J].西安交通大学学报,2014(1):123-126,132. |
| [7] | 张景贤;江东亮;林庆玲;陈忠明;黄政仁.通过凝胶注模成型和无压烧结制备碳化硅陶瓷[J].硅酸盐学报,2012(8):1154-1157. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%