研究了等轴组织BT14合金在200、400和600℃下应力松弛行为,并通过应力松弛过程中微观组织的变化研究应力松弛的微观机理.研究表明,200℃应力松驰变形中,有位错运动启动;400℃发现位错滑移带,这时应力松弛的微观机理均为位错滑移导致的微区塑性变形;600℃应力松驰变形中,发现亚晶界和位错网,其松弛机理为回复蠕变.
参考文献
| [1] | Froes F H.Titanium products and applications[J].Journal of Metals,1994(03):12-14. |
| [2] | 陈春奎;黄勇坚;王以璠 等.钛和钛合金钣金零件的热校形[J].金属科学与工艺,1987,4(02):89-100. |
| [3] | 李昕.弹性与非弹性的测量和应用[M].北京:冶金工业出版社,1999 |
| [4] | 张新明,毛新平,邓至谦,范波,周卓平,曹金荣.铍铜带材弯曲应力松弛的力学行为[J].中国有色金属学报,2001(06):988-992. |
| [5] | 平修二;郭廷玮.金属材料的高温强度.理论.设计[M].北京:科学出版社,1983 |
| [6] | Evans W J;Harrison G F.Power law steady state creep in α/β titanium alloys[J].Journal of Materials Science,1983(18):3449-3455. |
| [7] | Sridhar G;Kutumbarao V V;Sarma S .The influence of heat treatment on the structure and properties of a near α titanium alloy[J].Metallurgical and Materials Transactions,1987,18A:877-891. |
| [8] | Weiss I;Froes F H;Eylen D et al.Modification of alpha morphology in Ti-6Al-4V by thermomedmical procsssing[J].Metall Tras A,1987,17:1935-1947. |
| [9] | Miler W H .Microstrueture,creep,and tensile deformation in Ti-6Al-2Nb-1Ta-0.8Mo[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1987,18:1451-1467. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%