采用超音速火焰喷涂技术在0Cr13Ni5Mo不锈钢基体上制备了铁基非晶涂层,研究了500%～800℃不同温度热处理对涂层的相组成和摩擦磨损性能的影响.从涂层的显微硬度分析、相组成分析、晶粒大小分析、以及摩擦磨损试验分析表明:随着热处理温度升高涂层的相结构及性能发生变化,在600℃时,涂层中析出大量的纳米硬质相,涂层的显微硬度和耐磨损性能也随之大幅提高;涂层的显微硬度在600℃时达到最大,耐磨性能在750℃时最好.
参考文献
| [1] | Kear B H;Skandan G;Sadangi R K et al.Thermal sprayed nanestructured W C/Co hardcoating[J].Journal of Thermal Spray Technology,2000,9(03):399-406. |
| [2] | You Wang;Stephen Jiang;Meidong Wang;Shihe Wang;T. Danny Xiao;Peter R. Strutt .Abrasive wear characteristics of plasma sprayed nanostructured alumina/titania coatings[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2000(2):176-185. |
| [3] | Sanjay Sampath .Micrestructural characteristics of plasma spray consolidated amorphous powders[J].Materials Science and Engineering,1993,A167:1-5. |
| [4] | Kishitake K;Era H;Otsubo F .Characterization of plasma sprayed Fe-17Cr-38Mo-4C amorphous coatings crystallizing at extremely high temperature[J].Journal of Thermal Spray Technology,1996,5(03):283-288. |
| [5] | 樊自拴;孙冬柏;俞宏英.等离子喷涂铁基非晶纳米晶复合涂层[A].辽宁大连,2003:55-59. |
| [6] | 潘继岗,樊自拴,孙冬柏,俞宏英,李辉勤,孟惠民,王旭东.超音速火焰喷涂制备钼基非晶纳米晶涂层的研究[J].中国表面工程,2004(06):22-26. |
| [7] | 樊自拴,孙冬柏,俞宏英,李辉勤,孟惠民,王旭东.等离子喷涂钼基非晶-纳米晶复合涂层的组织与性能[J].材料热处理学报,2005(02):90-93. |
| [8] | 等离子喷涂制备铁基非晶-纳米复合涂层[J].北京科技大学学报,2005(05):582-585. |
| [9] | 潘继岗,樊自拴,孙冬柏,俞宏英,李辉勤,王旭东,孟惠民.超音速火焰喷涂Fe基非晶合金涂层的性能研究[J].材料工程,2005(09):53-55. |
| [10] | 于会生,罗守福,王永瑞.化学沉积Ni-P及Ni-Cu-P合金镀层晶化行为的比较[J].材料工程,2002(04):19-23. |
| [11] | 蒋太祥,吴辉煌.化学镀镍-高磷合金的微观结构及晶化行为研究[J].高等学校化学学报,2001(06):976-979. |
| [12] | 牛振江,吴廷华,李则林.化学镀镍-高磷合金晶化行为的现场 XRD研究[J].物理化学学报,2003(08):705-708. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%