基于密度泛函理论的第一性原理平面波赝势方法研究了V掺杂Ni3Al合金的电子结构和点缺陷结构.通过计算与实验结果对比选择了适合Ni3Al合金计算的近似方法,计算了含有各个缺陷的晶胞的晶格常数,形成热和结合能,点缺陷的形成能和平衡浓度,态密度和电荷密度.计算结果表明:Ni3Al合金中反位缺陷较空位缺陷易形成,NiAl是Ni3Al合金中最主要的反位缺陷,Al位最易形成缺陷,在1400 K时,空位缺陷的浓度远远低于反位缺陷的浓度.V加入Ni3Al合金体系中能提高合金的稳定性.
参考文献
| [1] | Sheng L Y;Zhang W;Guo J T et al.[J].Intermetallics,2009,17:572. |
| [2] | Georgea E P;Liu C T;Linb H et al.[J].Materials Science and Engineering,1995,A192/193:277. |
| [3] | Zhao Y H;Hou H;Xu H et al.[J].Journal of Materials Science and Technology,2003,19(S):18. |
| [4] | Fu C L;Painter G S .[J].Acta Materialia,1997,45(02):481. |
| [5] | Song Yua;Chong-Yu Wang;Tao Yu et al.[J].Physica,2007,B396:138. |
| [6] | Hannes Schweiger;Olga Semenova;Walter Wolf .Energetics of point defect formation in Ni_3A1[J].Scripta materialia,2002(1):37-41. |
| [7] | Jiang C;Sordelet D J;Gleeson B .[J].Acta Materialia,2006,54:1147. |
| [8] | Shibuya S et al.[J].Intermetallics,2007,15:119. |
| [9] | 张静,陈铮,王永欣,卢艳丽,霍进良,甄辉辉,赵彦.微观相场法模拟Ni75Al5.3V19.7中L12和D022结构反位缺陷的演化[J].物理学报,2009(01):631-637. |
| [10] | R. Arroyave;D. Shin;Z.-K. Liu .Ab initio thermodynamic properties of stoichiometric phases in the Ni-Al system[J].Acta materialia,2005(6):1809-1819. |
| [11] | Mishin Y .[J].Acta Materialia,2004,52(06):145. |
| [12] | 陈律,彭平,李贵发,刘金水,韩绍昌.B2-RuAl点缺陷结构的第一原理计算[J].稀有金属材料与工程,2006(07):1065-1070. |
| [13] | 周惦武,彭平,胡艳军,刘金水.Mg-Ce化合物相结构稳定性的赝势平面波方法研究[J].稀有金属材料与工程,2006(06):871-875. |
| [14] | 陈律,彭平,韩绍昌.B2-YX（X=Cu,Rh,Ag,In）点缺陷结构及其基本物性的理论计算[J].稀有金属材料与工程,2007(12):2089-2093. |
| [15] | 石德珂.Fundamentals of Materials Science (材料科学基础)[M].北京:机械工业出版社,2003:95. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%