ZG42　CrMo缩松区疲劳裂纹的偏析和微裂纹的形成

金属学报, 1996, 32(10): 1056-1062.

ZG42　CrMo缩松区疲劳裂纹的偏析和微裂纹的形成

沈阳工业大学

东北大学

关键词：ＺＧ４２ＣｒＭｏ , porosity , fatigue crack deflection , microcrack.

FATIGUE CRACK DEFLECTION AND FORMATION OF MICROCRACKS IN POROSITY AREA OF ZG42CrMo

ZHAO Fangxin , ZHANG Yingjie , ZHANG Song , ZHAO Zuxin , YIN Shaokui , LI Decheng(Shenyang Research Institute of Foundry

Keywords： :ZG42CrMo , 缩松 , 疲劳裂纹偏折 , 微裂纹

测定了ＺＧ４２ＣｒＭｏ高周疲劳裂纹扩展速率，对疲劳裂纹扩展过程进行了金相追踪观察．用ＥＰＭ研究了缩松及其表面微裂纹和硫化物的形态．用ＴＥＭ研究了裂纹顶端位错组态和滑移特征．讨论了缩松对裂纹捕获和偏折对疲劳裂纹扩展的双重影响及微裂纹萌生的可能机制．

The fatigue crack propagation rates of ZG42CrMo and its porosity area were measured.The process of fatigue crack growth in porosity area was observed by using metallographic tracing method.Dislocation and slip at the tip of fatigue crack have been studied by using TEM.The morphologies of porosities and microcracks together with sulphide on the surface of porosities were researched by using EPM.Two effects of porosities which make crack deflection and catch crack on fatigue crack growth have been discussed.Possible mechanism of microcrack initiation has been analysed.

参考文献

[1]
[2]
[3]
[4]
[5]
[6]
[7]
[8]
[9]	ZhaoFX,WuYX．ZhangYJ,ChenM,ZhaoZX．In:AcademicCommitteeofICTD'95ed．,Proc3rdIntConfonTechnicalDiagnosticsandTechnicalSeminar,Jilin:OrganizingCommitteeofICTD'95,1995:2892赵芳欣,张瑛洁,尹绍奎,赵祖欣,张松．钢铁,1996

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网