The microstructure and wear behaviour of the thermite reaction coating produced by the hybrid laser claddingremelting on AA7075 aluminum alloy for the systems of Al-CuO-SiO2, Al-Cr2O3-SiO2, Al-Fe2O3-SiO2, and Al-TiO2-SiO2 were studied. The results of the X-ray diffraction (XRD) analysis show that in all the four reaction coatings, α-Al2O3 and γ-Al2O3 phases were present at the top surface, together with various intermetallic phases, the corresponding reduced metal and Al phase in the fusion zone. Under the dry sliding condition, the wear resistance, in terms of weight loss, of the laser-clad specimens was considerably higher than that of the untreated specimen. The predominant wear mechanism of the former specimens was abrasive wear, while for the latter, it was the adhesive wear that prevailed.
参考文献
| [1] | A. Dasari;S. Nayak;R. D. K. Misra .Surface characteristics and wear performance of laser surface engineered iron oxide coatings on cast aluminium alloy[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2002(9):1036-1040. |
| [2] | H R Geng;Y C Niu;X F Tian;C Z Chen X X Hou .[J].Journal of Materials Science and Technology,2001,17(z1):S115. |
| [3] | H C Man;S Zhang;F T Cheng;T M Yue .[J].Scripta Materialia,2002,46(03):229. |
| [4] | J S Selvan;K Subramanian;A K Nath;C Ramachandra S P Ravindranathan .[J].Laser Eng,1998,8(01):43. |
| [5] | Y D Kogan;Z S Sazonova;V D Aleksandrov;T M Borovskaya .[J].METAL SCIENCE AND HEAT TREATMENT,1991,33(9-10):772. |
| [6] | Y Q Fu;A W Batchelor .[J].Surface and Coatings Technology,1998,102(1-2):119. |
| [7] | L R Katipelli;A Agarwal;N B Dahotre .[J].Applied Surface Science,2000,153(2-3):65. |
| [8] | S Yang;N Chen;W J Liu;M L Zhong .[J].Materials Letters,2003,57(22-23):3412. |
| [9] | P H Chong;H C Man;T M Yue .[J].Surface and Coatings Technology,2001,145(1-3):51. |
| [10] | T. T. Wong;G. Y. Liang;B. L. He;C. H. Woo .Wear resistance of laser-clad Ni-Cr-B-Si alloy on aluminium alloy[J].Journal of Materials Processing Technology,2000(1/3):142-146. |
| [11] | K. Uenishi;K.F. Kobayashi .Formation of surface layer based on Al3Ti on aluminum by laser cladding and its compatibility with ceramics[J].Intermetallics,1999(5):553-559. |
| [12] | J Kelly;K Nagarathnam;J Mazumder .[J].Journal of Laser Applications,1998,10(02):45. |
| [13] | X B Zhou;J T M Dehosson .[J].J Phys Ⅳ,1993,3(C7):1007. |
| [14] | N B Dahotre;S Nayak;O O Popoola .[J].JOM-J Miner Met Mat S,2001,53(09):44. |
| [15] | S Nayak;H Wang;E A Kenik;I M Anderson N B Dahotre .[J].Materials Science and Engineering A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2005,390(1-2):403. |
| [16] | H C Man;Y Q Yang;W B Lee .[J].Surface and Coatings Technology,2004,185(01):74. |
| [17] | J T De Hosson;V Ocelik;U De Oliveira;S Seal N B Dahotre J Moore S Suryanarayana A Agarwal.Surface Engineering in Materials Science,Ⅱ[M].TMS,2003:197. |
| [18] | P H Chong;H C Man;T M Yue .[J].Surface and Coatings Technology,2002,154(2-3):268. |
| [19] | M Kaneta;K Matsuda;J Matsuda;A Utsumi .[J].WEAR,1992,156(01):161. |
| [20] | Hugh Baker.ASM Handbook,Alloy Phase Diagrams[M].ASM International,Metals Park,OH,1992:2.43,2.44,2.54. |
| [21] | T M Yue;K J Huang;H C Man .[J].Surface and Coatings Technology,2005,194(2-3):232. |
| [22] | Y C Dong;D R Yan;J J He;X Z Li W R Feng H Liu .[J].Surface and Coatings Technology,2004,179(2-3):223. |
| [23] | A H Wang;Z Y Tao;J M Fu;X Y Ma .[J].SURFACE AND COATINGS TECHNOLOGY,1992,52(02):141. |
| [24] | E Fernández;J M Cuetos;R Vijande;A Rincónt .[J].Tribology International,1996,29(06):477. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%