DECREASING PITTING SUSCEPTIBILITY OF PASSIVE FILMS ON X70 PIPELINE STEEL IN NaCl SOLUTIONS BY ILLUMINATION

金属学报(英文版), 2006, 19(2): 91-97.

^1, , ^2, , ^3, , ^4,

1.Department of Chemistry, Zhejiang University, Hangzhou 310027, China

2.Department of Chemistry, Zhejiang University, Hangzhou 310027, China

3.Department of Chemistry, Zhejiang University, Hangzhou 310027, China;State Key Laboratory for Corrosion and Protection of Metals, Institute of Metal Research, The Chinese Academy of Sciences, Shenyang 110016, China

4.Department of Chemistry, Zhejiang University, Hangzhou 310027, China;State Key Laboratory for Corrosion and Protection of Metals, Institute of Metal Research, The Chinese Academy of Sciences, Shenyang 110016, China

基金项目: 中国科学院资助项目(20373062)

DECREASING PITTING SUSCEPTIBILITY OF PASSIVE FILMS ON X70 PIPELINE STEEL IN NaCl SOLUTIONS BY ILLUMINATION

Keywords： X70 pipeline steel

The influence of UV illumination on passivity and pitting susceptibility on X70 pipeline steel in a borate buffer (pH=8.4) solution containing NaCl is described. It is observed that illumination of the sample leads to a decrease in its pitting susceptibility as indicated by pitting potential and incubation time measurements in chloride containing electrolytes. This effect is strongly dependent on the applied potential during passivation. The electronic properties of the passive films on X70steel were studied by Mott-Schottky analysis and photocurrent transient measurements. The results indicated that illumination during passivation led to modifications in the electronic properties of the passive films, mainly to a decrease of the bulk doping and an increase in the surface state density. The cause for the decrease in the pitting susceptibility is preliminary explained in terms of such modifications of the passive film.

参考文献

[1]	R G Wendt;W C Moshier;B Shaw;P Miller, D L Olson .[J].Corrosion,1994,50:819.
[2]	B A Shaw;G D Shaw;T L Fritz;B J Rees, W C Moshier .[J].Journal of the Electrochemical Society,1991,138:3288.
[3]	C N Cao.Corrosion Electrochemistrty Principle[M].北京:化学工业出版社,1994:232.
[4]	C B Breslin;D D Macdonald;J Sikora;E Sikora .[J].Electrochimica Acta,1997,42:137.
[5]	C B Breslin;D D Macdonald .[J].Electrochimica Acta,1998,44:643.
[6]	P Schmuki;H Bohni .[J].Electrochimica Acta,1995,40:775.
[7]	D D Macdonald;D F Heaney .[J].Corrosion Science,2000,42:1779.
[8]	C B Breslin;D D Macdonald;J Sikora;E Sikora .[J].Electrochimica Acta,1997,42:127.
[9]	Y. M. Zeng;J. L. Luo .Electronic band structure of passive film on X70 pipeline steel[J].Electrochimica Acta,2003(23):3551-3562.
[10]	L J Zhang;Z Zhang;F H Cao;J Q Zhang, J W Wang, C N Cao .[J].Acta Metallurgica Sinica,1998,34:1188.
[11]	L J Zhang;Master's Thesis .[D].杭州:浙江大学,2005.
[12]	J L Cao;W H Leng;J Q Zhang;C N Cao .[J].Acta Physico-Chimica Sinica,2004,20:735.
[13]	Z Szklarska-Simialowska .Pitting Corrosion of Metal[J].NACE Houston TX,1986,100
[14]	D D Macdonald .[J].Pure and Applied Chemistry,1999,71:951.
[15]	M Yang;L Chen;S Cai .[J].Corrosion,1997,53:11.
[16]	R Peat;L M Peter .[J].Journal of Electroanalytical Chemistry,1987,228:351.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

DECREASING PITTING SUSCEPTIBILITY OF PASSIVE FILMS ON X70 PIPELINE STEEL IN NaCl SOLUTIONS BY ILLUMINATION

参考文献