用聚醚砜对环氧树脂进行室温和超低温的增韧研究,测试了该环氧树脂体系在室温和超低温的断裂韧性、冲击强度、弯曲性能、拉伸性能和压缩性能.实验结果表明,在室温和液氮温度下,PES均能增加环氧树脂体系的断裂韧性(KIc), 但在液氮温度下,KIc的增加程度小于室温.在室温下,PES改性树脂体系的冲击强度基本不变,而在液氮温度下则明显增大.在液氮温度下,增韧体系的弯曲、压缩和拉伸性能比室温有更显著的降低.在室温,增韧体系的强度降低10%～22%,而在液氮温度下则下降15%～32%.在室温,增韧体系的模量没有明显减小,而在液氮温度下则下降了15%～32%.
参考文献
| [1] | MacKinnon A J;Jenkins S D;McGrail P T.[J].Macromolecules:3492-3499. |
| [2] | Akay M;Cracknell J G.[J].Journal of Applied Polymer Science,1994:663-688. |
| [3] | Yoon T H;Mcgrath J E.[J].Journal of Applied Polymer Science,2001:1504-1513. |
| [4] | Grimsley B W;Cano R J;Johnston N J.33rd International SAMPE Technical Conference[C].,2001:1597-1606. |
| [5] | Ueki T;Nojima K;Asano K.[J].Advances in Cryogenic Engineering:277-283. |
| [6] | Li·B·C.Fundamentals of Polymer Physics[M].北京:化学工业出版社,1999 |
| [7] | Yamaoka H;Miyata K;Yano O .[J].CRYOGENICS,1995,35:787-789. |
| [8] | MacKinnon A J;Jenkins S D;McGrail P T.[J].Journal of Applied Polymer Science,1995:2345-2355. |
| [9] | Yamanaka K;Inoue T.[J].POLYMER,1989:662-667. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%