采用固相反应法制备了稀土锆酸盐材料.通过XRD图谱和SEM对材料的显微结构进行分析,并测试了不同温度下材料的热膨胀系数.结果表明:稀土锆酸盐材料的热膨胀系数大约为11×10-6/℃,其值随着温度的升高而升高,升高的速率逐渐减小.随着原子序数的增大,热膨胀系数是逐渐减小的,这说明稀土锆酸盐材料的热稳定性是随着原子序数的增大逐渐增强的.
参考文献
| [1] | Miller R A .[J].Surface and Coatings Technology,1987,30(01):1. |
| [2] | Vassen R.;Cao X. .Zirconates as New Materials for Thermal Barrier Coatings[J].Journal of the American Ceramic Society,2000(8):2023-2028. |
| [3] | Padture NP;Gell M;Jordan EH .Materials science - Thermal barrier coatings for gas-turbine engine apptications [Review][J].Science,2002(5566):280-284. |
| [4] | Wu J;Wei X;Padture N P et al.[J].Journal of the American Ceramic Society,2002,85:3031. |
| [5] | Cao X Q;Vassen R;Stoever D .[J].Journal of the European Ceramic Society,2004,24:1. |
| [6] | Schulz U;Leyens C;Fritscher K et al.[J].Aerospace Science and Technology,2003,7:73. |
| [7] | Clarke DR. .Materials selection guidelines for low thermal conductivity thermal barrier coatings[J].Surface & Coatings Technology,2003(0):67-74. |
| [8] | 关振铎;张中太;焦云生.无机材料物理性能[M].北京:清华大学出版社,1998 |
| [9] | Kingery W D;Bowen H K;Uhlmann D R.陶瓷导论[M].北京:中国建筑工业出版社,1987 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%