研究了真空熔炼时熔体温度对类K445镍基高温合金铸态组织及硬度的影响.结果表明,熔体温度对合金的相种类没有影响,均由树枝状y基体、弥散分布于基体的γ'相、晶界和枝晶间的γ+γ'共晶、以及γ"、MC碳化物、少量M3B2硼化物等强化相组成;但随熔体温度的升高,枝晶逐渐细化,一次枝晶轴大量熔断;MC碳化物含量逐渐减少,γ+γ'共晶和γ"相逐渐增多;同时,随熔体温度的升高,合金的硬度不断提高.在1600℃保温时,合金组织中枝晶最细小、γ+γ'共晶和γ"含量最多、碳化物含量最少,且HB硬度达到最高值3.84 GPa.
参考文献
| [1] | Al-Jarba K A;Fuehs G E .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2004,373:255. |
| [2] | Tin S.;Pollock TM. .Phase instabilities and carbon additions in single-crystal nickel-base superalloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):111-121. |
| [3] | Razavi SH.;Mirdamadi S.;Szpunar J.;Arabi H. .Improvement of age-hardening process of a nickel-base superalloy, IN738LC, by induction aging[J].Journal of Materials Science,2002(7):1461-1471. |
| [4] | 李耀彪,孙晓峰,张承忠,殷凤仕,郑启,侯贵臣,于洋.冶炼工艺对M963合金高温持久性能的影响[J].机械工程材料,2003(04):18-20. |
| [5] | Liu Feng;Yang Gencang .[J].Journal of Materials Science,2002,37:2713. |
| [6] | 郑亮 .Ta和Ru对低铬高钨铸造镍基高温合金组织及性能的影响[D].西安:西安科技大学,2004. |
| [7] | 苏彦庆;郭景杰;刘贵仲.有色合金真空熔炼过程熔体质量控制[M].哈尔滨:哈尔滨工业大学出版社,2005:31. |
| [8] | 殷风仕;孙晓峰;李耀彪 et al.[J].金属学报,2003,39(01):75. |
| [9] | 王建明,袁超,牛建平,才庆魁,胡壮麒.高温精炼处理对铸造镍基高温合金组织与性能的影响[J].中国有色金属学报,2004(05):713-717. |
| [10] | 郑运荣;张德堂.高温合金与钢的彩色金相研究[M].北京:国防工业出版社,1999:153. |
| [11] | 殷凤仕,孙晓峰,侯贵臣,郑启,管恒荣,胡壮麒.熔体过热处理对M963合金凝固偏析的影响[J].稀有金属材料与工程,2004(06):659-661. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%