Texture evolution of ferritic hot rolled Ti-IF steel was investigated during cold rolling in the reduction from 15% to 85%. It was found that, α fibre intensified monotonously with the increase of the cold reduction, but γ fibre changed in a different way. As the cold reduction was in the range of 15%-35% or 45%-75%, γ fibre intensified. While the reduction was between 35%-45% or 75%-85%, the intensity of γ fibre reduced. γ fibre displayed the maximum intensity at 75% and the highest average plastic strain ratio due to the favorable recrystallization texture was obtained at this point.