采用共沉淀法,以NH4OH为沉淀剂制备了1％(原子分数)Nd3+:Gd3 Se2 Al3 O12前驱体,并在不同的温度下对前驱体进行煅烧.用X射线衍射(XRD)和红外光谱(FT-IR)技术对前驱体及煅烧后粉体的结构、微观形貌进行了研究.结果表明,前驱体在1000℃下煅烧n获得纯GSAG多晶相粉体.用X射线衍射宽化法估算粉体的平均晶粒尺寸为25 nm.通过X射线粉末衍射,用Rietveld全谱拟合方法对晶体结构进行了精修,得到1000℃下煅烧所得Nd:GSAG粉体的晶胞参数为a=b=c=1.24164(5)nm,α=β=y=90°.在室温下,测定了激发波长为808m的发射谱和检测波长为942 nm的激发谱.另外,测定了 942和1064 nm处的荧光衰减曲线,并用单指数函数进行了拟合,得到对应的荧光寿命分别为0.529和0.512 ms.
参考文献
| [1] | Wulfmeyer V;Bauer H;Di Girolamo P;Serio C .Comparison of active and passive water vapor remote sensing from space: An analysis based on the simulated performance of IASI and space borne differential absorption lidar[J].Remote Sensing of Environment: An Interdisciplinary Journal,2005(2):211-230. |
| [2] | Treichel R;Czeranowsky C;Ileri B;Petermann K,Huber C.Mixed garnet laser crystals for water vapour DIAL transmitter[A].Toulouse,France,2004:639. |
| [3] | Kallmeyer F;Dziedzina M;Schmidt D;Eichler H J,Treichel R,Nikolov S.Nd:GSAG laser for water vapor detection by LIDAR near 942 nm[A].San Jose,California,U.S.A,2007:64510J. |
| [4] | Kallmeyer F;Dziedzina M;Wang X;Eichler HJ;Czeranowsky C;Ileri B;Petermann K;Huber G .Nd : GSAG-pulsed laser operation at 943 nm and crystal growth[J].Applied physics, B. Lasers and optics,2007(2/3):305-310. |
| [5] | S.G.P. Strohmaier;H.J. Eichler;C. Czeranowsky;B. Ileri;K. Petermann;G. Huber .Diode pumped Nd:GSAG and Nd:YGG laser at 942 and 935 nm[J].Optics Communications: A Journal Devoted to the Rapid Publication of Short Contributions in the Field of Optics and Interaction of Light with Matter,2007(1):170-172. |
| [6] | Wang S;Wang X;Kallmeyer F;Chen J Eichler H J .Model of pulsed Nd:GSAG laser at 942 nm considering rate equations with cavity structure[J].Applied Physics B,2008,92:43. |
| [7] | Su J;Liu B;Xu L H;Zhang Q L Yin S T .Effective segregation during Czochralski growth and spectral properties of Nd3 + in GSAG crystal[J].Journal of Alloys and Compounds,2012,512:230. |
| [8] | 张英.掺钕钆钪铝石榴石的生长、光学特性和连续激光作用[J].激光与红外,1974(04):13. |
| [9] | 张乐潓.人工石榴石的研究、应用与发展[J].人工晶体,1985(02):110. |
| [10] | 翁诗甫.傅里叶变换红外光谱分析[M].北京:化学工业出版社,2010:325. |
| [11] | 彭文世;刘高魁.矿物红外光谱图集[M].北京:科学出版社,1982:306. |
| [12] | Wang S F;Gu F;Lu M K;Song C F Liu S W Xu D Yuan D R .Preparation and characterization of sol-gel derived ZnTiO,nanocrystals[J].Materials Research Bulletin,2003,38:1283. |
| [13] | Larson A C;Von Dreele R B .General structure analysis system(GSAS)[R].Los Alamos National Laboratory Report,2004. |
| [14] | 肖进,张庆礼,周文龙,谭晓靓,刘文鹏,殷绍唐,江海河,夏上达,郭常新.Nd3+：Gd3 Sc2Al3O12晶场能级及拟合[J].物理学报,2010(10):7306-7313. |
| [15] | Kaminskii A A.Crystalline Lasers:Physical Processes and Operating Schemes[M].Boca Raton:CRC Press,1996:145. |
| [16] | 左周,杨魁胜,李慧,祁宁.NaGd（W04）2：Yb3+,Tm3+纳米粉的制备与上转换发光性能[J].中国稀土学报,2012(01):73-77. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%