Plasma nitrocarburizing and plasma oxidizing treatments were performed to improve the wear and corrosion resistance of SKD 61 steel. Plasma nitrocarburizing was conducted for 12 h at 540℃ in the nitrogen,hydrogen and methane atmosphere to produce the ε-Fe,2-3(N,C) phase. The compound layer produced by plasma nitrocarburising was predominantly composed of ε-phase, with a small proportion of γ′-Fe4(N,C) phase.The thickness of the compound layer and the diffusion layer are about 10 μm and about 200μm, respectively.Plasma post oxidation was performed on the nitrocarburized samples with various oxygen/hydrogen ratio at constant temperature of 500℃ for 1 h. The very thin magnetite (Fe3O4) layer of 1-2μm in thickness on top of the compound layer was obtained. Anodic polarization test revealed that plasma nitrocarburizing process contributed a significant improvement of corrosion resistance of SKD 61 steel. However, the corrosion characteristics of the nitrocarburized compound layer was deteriorated by oxidation treatment.
参考文献
| [1] | T Bell;Y Sun;A Suhadi .[J].Vacuum,2000,59:14. |
| [2] | S Hoppe .[J].Surface and Coatings Technology,1998,98:1199. |
| [3] | Insup Lee .[J].Surface and Coatings Technology,2004,188-198:66. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%