用粉末冶金法(磁场压制烧结)制备(Mn_(1-x)Fe_x)_5Sn_3(x=0.1～0.5)合金,对其晶体结构、居里温度进行研究.室温XRD分析表明,该系列合金均保持Mn_5Sn_3的InNi_2型相结构,计算发现合金的晶格常数随着x量增大而减小.通过M-T曲线测量结果表明:居里温度T_C在室温附近244～391 K连续可调,且随着Fe含量的增加而提高,居里温度随成分近似呈线性变化:成分为(Mn_(0.70)Fe_(0.30))_5Sn_3合金的居里温度为295 K,在外加磁场为0～1.5 T下,最大磁熵变约为0.87 J·(kg·K)~(-1),是一种成本低廉的室温磁制冷候选材料.
(Mn_(1-x)Fe_x)_5Sn_3 (x=0.1-0.5) alloys were prepared by powder metallurgy method with magnetic field pressing and sintering. The crystal structure, Curie temperature and magnetic entropy change of the alloys were studied. XRD patterns reveal that all samples of this system maintain a hexagonal In Ni_2-type structure with space group P6_3/mmc. The lattice parameter and cell volumes of the (Mn_(1-x)Fe_x)_5Sn_3 alloys decrease with x increasing by calculation, while the Curie temperature of these alloys increases almost linearly and is tunable continually from 244 K to 391 K by M-T curves. The Curie temperature of (Mn_(0.70)Fe_(0.30))_5Sn_3 is about 295 K close to room temperature, and the maximum magnetic entropy change is 0.87(kg·K)~(-1) with a field change form 0 to 1.5 T. The curve of magnetic entropy change of (Mn_(0.70)Fe_(0.30))_5Su_3 is flat in a wide temperature range. It is indicated that the (Mn_(1-x)Fe_x)_5Sn_3 alloy is a suitable candidate with low cost for Ericsson cycle.
参考文献
| [1] | 孔俊峰,侯雪玲,李士涛,张少杰.工质材料GdDyFe磁热效应的研究[J].稀有金属材料与工程,2006(08):1251-1253. |
| [2] | Ao WQ;Jian YX;Liu FS;Feng XW;Li JQ .The influence of gallium on magnetocaloric effect in Gd60Tb40 alloys[J].Journal of Magnetism and Magnetic Materials,2006(1):120-123. |
| [3] | Tegus O;Bruck E;Buschow K H J et al.[J].Nature,2002,415:150. |
| [4] | Pecharsky VK;Gschneidner KA .Giant magnetocaloric effect in Gd-5(Si2Ge2)[J].Physical review letters,1997(23):4494-4497. |
| [5] | Hu F X;Shen B G;Sun J R et al.[J].Applied Physics Letters,2002,80:826. |
| [6] | Hu F X;Shen B G;Sun J R .[J].Applied Physics Letters,2000,76:3460. |
| [7] | Songlin;Dagula;O. Tegus .Magnetic phase transition and magnetocaloric effect in Mn_(5-x)Fe_xSi_3[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2002(1/2):249-252. |
| [8] | Zhao F Q;Dagula W;Tegus O et al.[J].Journal of Alloys and Compounds,2006,416:43. |
| [9] | Murthy N S S;Begum R J;Srinivasan B S .[J].Physics Letters,1965,15:225. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%