以辛酸亚锡为催化剂,通过熔融聚合的方法制备了己内酯/乙交酯/丙交酯三元嵌段聚酯共聚物,采用GPC、FT-IR、1H NMR、XRD等方法对聚酯共聚物的结构进行了表征,并测试了聚酯共聚物在天然海水中的吸水性能和降解性能.用HDI三聚体对所合成聚酯共聚物进行固化,测试固化后树脂的力学性能及降解性能.结果表明:通过调节树脂中己内酯链段含量,可控制固化树脂的力学弹性;在天然海水中的降解实验表明,随着己内酯链段含量降低,固化树脂降解速率加快,平衡后的水解速率基本维持在5～10μg/(cm2·d).
参考文献
| [1] | 颜东洲;贾成功.防污涂料的应用和技术进展[J].化工科技市场,2002(12):21-24. |
| [2] | Yebra DM;Kiil S;Dam-Johansen K.Antifouling technology - past, present and future steps towards efficient and environmentally friendly antifouling coatings[J].Progress in Organic Coatings: An International Review Journal,20042(2):75-104. |
| [3] | Fay F;Renard E;Langlois V;Linossier I;Vallee-Rehel K.Development of poly(epsilon-caprolactone-co-L-lactide) and poly(epsilon-caprolactone-co-delta-valerolactone) as new degradable binder used for antifouling paint[J].European Polymer Journal,200711(11):4800-4813. |
| [4] | Fay F;Linossier I;Peron JJ;Langlois V;Vallee-Rehel K.Antifouling activity of marine paints: Study of erosion[J].Progress in Organic Coatings: An International Review Journal,20073(3):194-206. |
| [5] | 何庆光;王晶晶;叶章基;任润桃.防污涂料用可降解聚氨酯树脂基料的合成研究[J].材料开发与应用,2009(6):19-23,32. |
| [6] | 胡晶;王晶晶;黄从树;秦岩;任润桃.丙交酯/己内酯聚酯共聚物在天然海水中水解行为研究[J].涂料工业,2012(3):44-47. |
| [7] | 邓冰锋;黄志雄;黄从树;任润桃;王晶晶;江学志.己内酯/乙交酯嵌段共聚物的合成及水解行为研究[J].涂料工业,2013(3):5-11. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%