为了扩大硅烷与无机盐复合钝化的应用范围，简化工艺，降低成本，以硅烷偶联剂为主成膜物，磷酸盐、氟钛酸盐作钝化剂，Na2MoO4和NH4VO3作缓蚀剂，一步钝化制备了无机-有机硅烷复合钝化膜。采用扫描电子显微镜、硫酸铜点滴腐蚀、盐水浸泡、中性盐雾试验、电化学测试等技术对钝化膜层的微观形貌、性能进行了分析。结果表明：无机。有机硅烷复合钝化膜在锌层表面起到了化学和物理的屏障作用，可以阻止腐蚀过程中的极化反应和锌的溶解，增强镀锌钢板的耐蚀性；无机-有机硅烷复合钝化膜的腐蚀面积小于5％，极化阻抗达到9kΩ，耐蚀性能接近铬酸盐钝化膜。
参考文献
| [1] | 卢锦堂;孔纲;车淳山 等.用于镀锌层防白锈的无机.有机硅烷复合钝化液及其涂覆方法[P].中国,200610123994.1,2007-06-06. |
| [2] | Montemor M F;Ferreira M G .Cerium salt activated nanoparticles as fillers for silane fillms:Evaluation of the corrosion inhibition performance on galvanised stgel substrates[J].Electrochimica Acta,2007,52:6976-6987. |
| [3] | Zhu DQ.;van Ooij WJ. .Corrosion protection of metals by water-based silane mixtures of bis-[trimethoxysilylpropyl]amine and vinyltriacetoxysilane [Review][J].Progress in Organic Coatings: An International Review Journal,2004(1):42-53. |
| [4] | M. G. S. Ferreira;R. G. Duarte;M. R. Montemor;A. M. R. Simoes .Silanes and rare earth salts as chromate replacers for pre-treatments on galvanised steel[J].Electrochimica Acta,2004(17/18):2927-2935. |
| [5] | 周渝生.无铬钝化技术研究的进展[J].钢铁,2003(04):68-71. |
| [6] | PENG Tianlan,MAN Ruilin.Rare earth and silane as chromate replacers for corrosion protection on galvanized steel[J].稀土学报（英文版）,2009(01):159-163. |
| [7] | KONG Gang,LU Jintang,WU Haijiang.Post treatment of silane and cerium salt as chromate replacers on galvanized steel[J].稀土学报（英文版）,2009(01):164-168. |
| [8] | 徐斌,满瑞林,倪网东,胡豫,曹晓燕,颜莎,史燕.镀锌钢板表面硅烷、铈盐复合膜的制备及耐腐蚀性能研究[J].涂料工业,2007(12):46-50. |
| [9] | 张金涛,杨春勇,潘亮,李春东.2A12铝合金表面铈盐掺杂硅烷杂化膜在3.5%NaCl溶液中耐蚀性能的电化学研究[J].金属学报,2008(11):1372-1377. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%