The influences of alloying elements W, Mo, Cr, and Nb on retained β phase in 47Al based near γ-TiAl alloys have been studied. The results reveal that the amount of retained β phase is increased by the addition of Cr, Mo, W in rising rank, although the distribution of β phase in Cr-bearing alloys is different from that of Mo- or W-bearing alloys. For Nb-doped alloys, no retainedβwas found even when 5 at.pct Nb was added. The as-cast microstructural features and the distribution of theβphase in the different alloy families were compared and interpreted in terms of the different segregation behaviour of these elements in Ti.