A laboratory study was undertaken to investigate drying shrinkage and cracking sensitivity subjected to restrained shrinkage of mortar containing fly ash (FA), granulated blast-furnace slag (GBFS) and silica fume (SF). Six mortar mixtures including control Portland cement (PC) and FA,GBFS and SF mortar mixtures were prepared. FA replaced the cement on mass basis at the replacement ratios of 20% and 35%, GBFS replaced the cement at the replacement ratios of 40%, SF replaced the cement at the replacement ratios of 8% and the blended mixtures with 20% FA, 20% GBFS and 8% SF. Water-cementitious materials ratio and sand-cementitious materials ratio were 0.4 and 2.0 for all mixtures, respectively. The mixtures were cured at 65% relative humidity and 20℃. The drying shrinkage value, initial cracking time and cracking width of the mortar samples were measured. The results show that all the mortar mixture containing FA exhibited the decrease of drying shrinkage.Moreover, initial cracking time was markedly delayed, and the crack width of the initial crack was reduced. However, the incorporations of various ratios of GBFS and SF led to an increase of drying shrinkage, initial cracking time and cracking width as compared to control mixture.
参考文献
| [1] | Frank Collins;J G Sanjayan .Cracking Tendency of Alkali-activated Slag Concrete Subjected to Restrained Shrinkage[J].Cement and Concrete Research,2001,30(05):791-798. |
| [2] | 亓萌,李宗津,马保国.Shrinkage and cracking behavior of high performance concretes containing chemical admixtures[J].浙江大学学报(英文版),2002(02):188-193. |
| [3] | Mehmet Gesoglu;Turan Ozturan;Erhan Guneyisi .Shrinkage cracking of lightweight concrete made with cold-bonded fly ash aggregates[J].Cement and Concrete Research,2004(7):1121-1130. |
| [4] | Salah A.altoubat;David A.Lange .Creepk, shrinkage, and cracking of restrained concrete at early age[J].ACI materials journal,2001(4):323-331. |
| [5] | P P Kiaai .Proposed Test to Determine Cracking Potential due to Drying Shrinkage of Concrete[J].Concrete Construction,1985,30(09):77-78. |
| [6] | Zhen He;Xiangming Zhou;Zongjin Li.New Experimental Method for Studying Early-Age Cracking of Cement-Based Materials[J].Aci Materials Journal,2003:98. |
| [7] | V M Malhotra .Concrete Ring for the Determination of Tensile Strength of Concrete[J].Aci Materials Journal,1970,77(04):354-357. |
| [8] | Banthia N;CYan;Mindess S .Restrained Shrinkage Cracking in Fiber Reinforced Concrete:a Novel Test Technique[J].Cement and Concrete Research,1996,26(01):9-14. |
| [9] | 高小建,何忠茂,杨英姿,周智,巴恒静.周边约束状态下板式混凝土早期开裂及收缩应变的分布[J].硅酸盐学报,2004(03):334-339. |
| [10] | Chan W.W.J.;Wu C.M.L. .Durability of concrete with high cement replacement[J].Cement and Concrete Research,2000(6):865-879. |
| [11] | Jiangyuan Hou;DDL Chung .Effect of Admixtures in Concrete on the Corrosion Resistance of Steel Reinforced Concrete[J].Corrosion Science,2000,42:1489-1507. |
| [12] | MA Baoguo,LI Jinzong,PENG Jun.INFLUENCE OF MINERAL ADMIXTURES ON MECHANICAL PROPERTIES OF HIGH-PERFORMANCE CONCRETE[J].武汉工业大学学报(英文版),1999(02):1-7. |
| [13] | MA Baoguo.SULFATE RESISTANCE MECHANISM OF HIGH-PERFORMANCE CONCRETE CONTAINING NCI[J].武汉工业大学学报,1999(01):6-15. |
| [14] | Ma Liyuan;Yao Yan .Research on Shrinkage Cracking Tendency of High-strength Concrete Containing Fly Ash[J].Concrete,2002,152(06):34-33. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%