利用氧氮分析仪和大样电解法对某厂采用210 t BOF-220 t LF-CC所生产的低碳铝镇静钢不同浇铸长度头坯夹杂物进行研究，并与正常坯相比较，得到结论如下：随着浇铸长度的增加，头坯中w（T [O ]），w（[N ]）和大型夹杂物数量均逐渐下降；头坯中夹杂物主要为TiN，SiO2，Al2 O3-SiO2和Al2 O3-MgO-CaO复合夹杂物，另外还发现少量的 Mg O夹杂物；头坯夹杂物数量增加的主要原因是钢水二次氧化、中间包覆盖剂和结晶器保护渣卷入；另外，钢包引流砂和中间包内衬也是导致头坯中夹杂物数量增加的原因。建议该厂该低碳铝镇静钢头坯的切废长度为大于4．0 m。
The inclusions in first slab of low carbon aluminium killed steel produced by 220 t BOF-220 t LF-CC and the comparative analysis with the inclusions of normal slab were studied by means of Oxygen and Nitrogen Analyzer and electroanalysis.The results are as follows:w(T[O]),w([N])and large-inclusions were generally decreasing with increasing of length;the inclusions were mainly TiN,SiO2 ,Al2 O3-SiO2 and Al2 O3-MgO-CaO complex inclu-sions;a small amount of MgO inclusions were also found.The reasons for the increasing were mainly reoxidation and entanglement of tundish covering flux and mold powder.Ladle filler sand and tundish lining can also make the inclusions increasing.The recommendation was that the length of slit should be more than 4.0 m.
参考文献
| [1] | 崔衡,岳峰,包燕平,王敏,吴维双.IF钢连铸头坯洁净度研究[J].钢铁,2010(03):38-41. |
| [2] | 安航航,韩传基,高仲,陶金明,包燕平,李太全.X70管线钢头坯质量的研究[J].钢铁研究,2011(01):31-34. |
| [3] | 彭其春,于学森,段雯君,熊伟,盛喜松,林利平,梁建伟.低碳钢头坯洁净度研究[J].武汉科技大学学报（自然科学版）,2012(03):164-168. |
| [4] | 杨文,薛勇强,曹晶,王新华,王万军.低碳铝镇静钢头坯洁净度研究[J].钢铁,2011(09):34-39. |
| [5] | 栗红,温铁光,孙群,陈本文,常桂华.管线钢浇次头坯夹杂物控制[J].鞍钢技术,2011(04):18-22. |
| [6] | 周琦.减少连铸头坯气孔的生产实践[J].武钢技术,2010(06):40-42. |
| [7] | 彭其春,于学森,熊伟,盛喜松,罗传清,刘俊.不同浇铸阶段低碳钢连铸板坯洁净度研究[J].中国冶金,2012(08):17-21. |
| [8] | 彭其春,于学森,熊伟,周明伟,张亮洲,周剑丰.高强钢尾坯洁净度[J].物理测试,2012(06):1-4. |
| [9] | 杨文,薛勇强,曹晶,王新华,王万军.低碳铝镇静钢头坯洁净度研究[J].钢铁,2011(09):34-39. |
| [10] | 唐海燕,李京社,杨树峰,孙开明,温德松.EAF-LF/VD-CC工艺生产压力容器钢的洁净度研究[J].钢铁,2008(01):30-32,54. |
| [11] | 张广军,陈玉辉.管坯钢夹杂物成因分析及工艺控制[J].炼钢,2006(06):1-4. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%