通过周浸腐蚀试验、电化学测量、锈层微观分析等方法研究了不同Cr含量耐候钢在模拟工业大气环境中的腐蚀行为.结果表明:随着耐候钢Cr含量增加,Cr在锈层中明显富集,促使锈层更加致密,减小了阳极溶解反应电流密度;其表面锈层的电阻Rr及反应电阻Rt均呈增大趋势,锈层的腐蚀电位正移,自腐蚀电流密度减小,极化曲线的阳极部分明显受到了阻碍,从而提高了耐候钢的耐蚀性.
参考文献
| [1] | Pedro Albrecht;Terry T. Hall .Atmospheric Corrosion Resistance of Structural Steels[J].Journal of Materials in Civil Engineering,2003(1):2-24. |
| [2] | H. E. Townsend .Effects of alloying elements on the corrosion of steel in industrial atmospheres[J].Corrosion: The Journal of Science and Engineering,2001(6):497-501. |
| [3] | Miki C .High strength and high performance steels and their use in bridge structures[J].Journal Constructional Steel Research,2002,58:43-20. |
| [4] | 杨景红,刘清友,王向东,李向阳,孙冬柏.耐候钢及其腐蚀产物的研究概况[J].中国腐蚀与防护学报,2007(06):367-372. |
| [5] | Masato Yamashita .Structure of Protective Rust Layers Formed on Weathering Steels by Long-term Exposure in the Industrial Atmospheres of Japan and North America[J].ISIJ International,1998(3):285-290. |
| [6] | Kamimura T;Stratmann M .The influence of chromium on the atmospheric corrosion of steel[J].Corrosion Science,2001,43(03):429-447. |
| [7] | 张全成,吴建生,郑文龙,王建军,陈家光,李爱柏,杨晓芳.合金元素的二次分配对耐钢抗大气腐蚀性能的影响[J].材料保护,2001(04):4-5. |
| [8] | 王博,郑春玉,郑艳,王德永,刘承军,姜茂发.高铬耐候钢的电化学行为研究[J].腐蚀科学与防护技术,2009(04):362-364. |
| [9] | 郝献超,肖葵,张汉青,董超芳,李晓刚.模拟海洋大气环境下Cu和Cr对耐候钢耐腐蚀性能的影响[J].材料保护,2009(01):21-23,43. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%