对一种钒微合金TRIP钢进行了热轧试验,并研究其微观组织特征及力学性能.结果表明,将终轧温度控制在Ae3附近,热轧后的钒微合金TRIP钢具有由铁素体,粒状贝氏体和一定量残余奥氏体组成的复相组织.EBSD分析结果表明,其中75%以上的铁素体晶粒尺寸在l-6 μm;绝大多数晶界取向差角度位于29°-60°.当终轧温度为830℃.终冷温度为650℃时,实验钢的综合力学性能较为优异,抗拉强度为1015 MPa,延伸率为19.5%,加工硬化指数为0.24.
参考文献
[1] | P.J.Jacques,E.Girault,A.Mertens,B.Verlinden,J.van Humbeeck,F.Delannay,The development of cold-rolled TRIP-assisted multiphase steels.Al-alloyed TRIPassisted multiphase steels,ISIJ International,41(9),1068(2001) |
[2] | Mahieu,J.Maki,B.C.De Cooman,S.Claessens,Phase transformation and mechanical properties of Si-free CMnAl transformation-induced plasticity-aided steel,Metallur Mater Trans A,33A,2573(2002) |
[3] | M.De Meyer,D.Vanderschueren,B.C.De Cooman,The influence of the substitution of Si by Al on the properties of cold rolled C-Mn-Si TRIP steels,ISIJ International,39(8),813(1999) |
[4] | Y.Chen,L.H.Wang,L.G.Dong,F.P.Li,Y.Zhang,Effects of Aluminum on microstructures and mechanical properties of hot-rolled TRIP steels,Proceedings of Sino-Swedish Structural Materials Symposium,368(2007) |
[5] | J.Maki,J.Mahieu,B.C.De Cooman,S.Claessens,Galvanisability of silicon-free CMnAI TRIP steels,Mater Sci Technol,19,125(2003) |
[6] | B.C.De Cooman,Structure + properties relationship in TRIP steels containing carbide-free bainite,Current Opinion in Solid State and Materials Science,8,285(2004) |
[7] | A.Basuki,E.Aernoudt,Effect of deformation in the intercritical area on the grain refinement of retained austenite of 0.4C TRIP steel,Scipta Materialia,40,1003(1999) |
[8] | Y.Sakuma,O.Matsumura,O.Akisue,Influence of C content and annealing temperature on microstructure and mechanical properties of 400℃ transformed steel containing retained anstenite,ISIJ International,31(11),1348(1991) |
[9] | E.V.Pereloma,I.B.Timokhina,P.D.Hodgson,Transformarion behaviour in thermomechanically processed CMn-Si TRIP steels with and without Nb,Materials Science and Engineering A,273-275,448(1999) |
[10] | E.V.Pereloma,K.F.Russell,M.K.Mitler,I.B.Timokhina,Effect of pre-straining and bake hardening on the microstructure of thermomechanically processed CMnSi TRIP steels with and without Nb and Mo aditions,Scripta Materialia,58,1078(2008) |
[11] | R.C.Thomson,M.K.Miller,Carbide precipitation in martensite during the early stages of tempering Crand Mo-containing low alloy steels,Acta mater,46(6),2203(1998) |
[12] | S.C.Balk,S.Kim,Y.S.Jin,O.Kwon,Effects of alloying elements on mechanical properties and phase transformation of cold rolled TRIP steel sheets,ISIJ International,41(3),290(2001) |
[13] | S.J.Kim,C.G.Lee,T.H.Lee,C.S.Oh,Effects of copper addition on mechanical properties of 0.15C-1.5Mn-1.5Si TRIP-aided multiphase cold-rolled steel sheets,ISIJ International,42(12),1452(2002) |
[14] | S.Jiao,F.ttassani,R.L.Donaberger,E.Essadiqi,S.Yue,The effect of processing history on a cold rolled and annealed Mo-Nb microalloyed TRIP steel,ISIJ International,42(3),299(2002) |
[15] | H.C.Chen,H.Era,M.Shimizu,Effect of phosphorus on the formation of retained unstenite and mechanical properties in Si-containing low-carbon steel sheet,Metallurgical Transacyions,20A,437(1989) |
[16] | E.Jimenez-Melero,N.H.van Dijk,L.Zhan,J.Sietsma,S.E.Offerman,J.P.Wright,S.van der Zwaag,The effect of aluminium and phosphorus on the stability of individual austenite grains in TRIP steels,Acta Materialia,57,533(2009) |
[17] | K.A.Taylor,Solubility products for titanium-,vanadium-,and niobium-carbide in ferrite,Scripta Metall Mater,32(1),7(1995) |
[18] | V.V.Popov,M.I.Goldshteyn,A.Y.Akeelrod,Predicting the dispersion hardening effect in ferrite-pearfite normalized steels modified with vanadium,Phys Met & Metall,70(1),145(1990) |
[19] | W.Shi,L.Li,C.X.Yang,R.Y.Fu,L.Wang,P.Wollants,Strain-induced transformation of retained austenite in tow-carbon low-silicon TRIP steel containing aluminum and vanadium,Materials Science and Engineering A,429,247(2006) |
[20] | A.Zarei-hanzaki,S.Yus,Ferrite formation characteristics in Si-Mn TRIP steels,ISIJ International,37(6),583(1997) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%