用超音速氧燃料热喷涂在铁基合金上制备热障涂层粘结层,用大气等离子热喷涂技术制备陶瓷层.研究了高温氧化后其界面化合物和残余应力的演变.结果表明,随着高温氧化的进行,TGO和BC/基体界面均有氧化物生成,但生长形貌和趋势并不一致.TGO由Al2O3层与尖晶石层组成;BC/基体界面氧化物为单一Al2O3,且存在层状和块状两种形貌.合金的热化学动力学引起元素Co和Ni向基底扩散比较严重,Al元素扩散止于界面氧化物层,基本不向铸铁基底扩散,Fe元素会向粘结层方向扩散.TGO残余应力的演化分为0～15 h和15～100 h 2个阶段,且残余应力与TGO的凹凸生长形貌及其物相组成密切相关;而BC/基体界面单一氧化物的残余应力基本稳定,不受其生长形貌影响.
参考文献
| [1] | Bouzakis KD.;Lontos A.;Michailidis N.;Knotek O.;Lugscheider E.;Bobzin K.;Etzkorn A. .Determination of mechanical properties of electron beam-physical vapor deposition-thermal barrier coatings (EB-PVD-TBCs) by means of nanoindentation and impact testing[J].Surface & Coatings Technology,2003(0):75-80. |
| [2] | Padture NP;Gell M;Jordan EH .Materials science - Thermal barrier coatings for gas-turbine engine apptications [Review][J].Science,2002(5566):280-284. |
| [3] | Chen WR;Wu X;Marple BR;Nagy DR;Patnaik PC .TGO growth behaviour in TBCs with APS and HVOF bond coats[J].Surface & Coatings Technology,2008(12):2677-2683. |
| [4] | Toscano J;Vassen R;Gil A;Subanovic M;Naumenko D;Singhelser L;Quadakkers W .Parameters affecting TGO growth and adherence on MCrAly-bond coats for TBC's[J].Surface & Coatings Technology,2006(7):3906-3910. |
| [5] | Clarke DR;Christensen RJ;Tolpygo V .The evolution of oxidation stresses in zirconia thermal barrier coated superalloy leading to spalling failure[J].Surface & Coatings Technology,1997(1/3):89-93. |
| [6] | Ke PL;Wang QM;Hua WG;Gong J;Sun C;Zhou YC .Stresses and microstructural development of thermal barrier coatings using AIP/D-gun two-step processing[J].Journal of the American Ceramic Society,2007(3):936-941. |
| [7] | He J.;Clarke DR. .DETERMINATION OF THE PIEZOSPECTROSCOPIC COEFFICIENTS FOR CHROMIUM-DOPED SAPPHIRE[J].Journal of the American Ceramic Society,1995(5):1347-1353. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%