某型号电热水器Incoloy800和840合金加热管发生爆管现象及漏电事故.通过临界点蚀温度测试(CPT)、极化曲线测量等方法研究了氯离子浓度对加热管材料点蚀性能的影响,确定了安全的氯离子浓度范围;比较了加热管制作工艺处理前后管材的点蚀性能以及显微组织形貌,确定了加热管制造工艺对合金点蚀性能的影响.结果表明,爆管主要是由于过高的氯离子浓度引起点蚀诱发应力腐蚀开裂.
参考文献
| [1] | 李岩,方可伟,刘飞华.Cl-对304L不锈钢从点蚀到应力腐蚀转变行为的影响[J].腐蚀与防护,2012(11):955-959. |
| [2] | 孔德生;杨武 .介质条件对核电用镍基合金传热管SCC的影响[J].腐蚀与防护,1997,28(1):15-18,20. |
| [3] | H.L. Pan;S.H. Tang;J.W. Hao .Failure analysis of a rotating cantilever shaft in chloride corrosive environment[J].Engineering failure analysis,2006(4):646-655. |
| [4] | T.M. Ahmed;A. Alfantazi;J. Budac .Failure analysis of 316L stainless steel tubing of the high-pressure still condenser[J].Engineering failure analysis,2009(5):1432-1441. |
| [5] | 吴玮巍,蒋益明,廖家兴,钟澄,郭峰,李劲.0Cr25Ni7Mo4、316与304不锈钢临界点蚀温度研究[J].腐蚀科学与防护技术,2006(04):285-288. |
| [6] | MERELLO R;BOTANA F J;BOTAELLA J et al.Influence of chemical composition on the pitting corrosion resistance of non-standard low-Ni high-Mn-N duplex stainless steels[J].Corrosion Science,2003,45(5):909-921. |
| [7] | 王文明,张毅.Cl~-浓度对双相钢和镍基合金腐蚀速率的影响[J].腐蚀与防护,2012(07):596-600. |
| [8] | M. Suresh Kumar;M. Sujata;M.A. Venkataswamy .Failure analysis of a stainless steel pipeline[J].Engineering failure analysis,2008(5):497-504. |
| [9] | A. Saad Abou-elazm;I. El Mahallawi;R. Abdel-karim .Failure investigation of secondary super-heater tubes in a power boiler[J].Engineering failure analysis,2009(1):433-448. |
| [10] | 李巨峰,韩建成,吴志军,王毅,石长仁,张雁鹏,于化合.Incoloy800H传热管抗晶间腐蚀性能研究[J].核动力工程,2012(04):50-53,63. |
| [11] | 王小莉,梁玉国,张骥.镍基合金材料耐晶间腐蚀试验各种判定方法的探讨[J].理化检验-物理分册,2006(12):617-620. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%