用自制的电磁离心铸造机,在离心机转速为960r/min,磁场强度分别为0.05、0.10、0.15、0.20T的条件下,制备了高碳高速钢,试验研究了不同磁场强度下的高碳高速钢的铸态组织和热处理后的组织与性能。结果表明：随着磁场强度的增加,高碳高速钢的铸态组织中角状、点状碳化物的分布逐渐趋于均匀、弥散,共晶碳化物呈现出先减少、变短,后增加、变长的趋势;热处理后组织中的共晶碳化物变细、变短,且在磁场强度为0.15T的试样中硬度、冲击韧度和耐磨性能达到最佳。
The high carbon high speed steel （HC-HSS） was made by self-made centrifugal casting machine with various magnetic flux density （0.05-0.20 T） and at the rotational speed 960 r/min. The influence of magnetic flux density of electromagnetic centrifugal casting machine on microstructure and properties of high carbon high speed steel （HC-HSS） was investigated. The results show that the angular, granular carbides of as-cast HC-HSS are well-distributed in the steel matrix and the eutectic carbides decreases first and then increases as the magnetic flux density increased. After heat treatment, the eutectic carbides become thin and short. The test specimen have high hardness, impact toughness and excellent relative wear resistance when the magnetic field strength reaches to 0. 15 T.
参考文献
| [1] | M.A. de Carvalho;R.R. Xavier;C. da Silva Pontes Filho .Microstructure, Mechanical Properties and Wear Resistance of High Speed Steel Rolls for Hot Rolling Mills[J].Iron & Steelmaker,2002(1):27-32. |
| [2] | Taku TANAKA;Takayuki KOIE;Masatoshi AYAGAKI .High Speed Steel Type Cold Rolling Mill Roll by Continuous Pouring Process for Cladding[J].NIPPON STEEL TECHNICAL REPORT,2002(86):80-85. |
| [3] | Xin Z;Perks M C.Centrifugal Casting of HSS Roll for Narrow Strip and Rod Mills[A].Pennsylvania:The Iron and Steel Society,2000:183. |
| [4] | 符寒光;邢建东.高速钢轧辊制造技术[M].北京:冶金工业出版社,2007 |
| [5] | 符寒光,邢建东.离心铸造高速钢轧辊铸造缺陷形成与控制技术研究[J].铸造技术,2004(11):859-861. |
| [6] | Asai S;Yasui K;Muchi I.Effects of Electric and Magnetic Forces on the Solidification Structure[J].ISIJ Interational,1978(18):754. |
| [7] | Kobayashi S;Ishimura S;Yoshihara M.Factors Affect ing Equiaxed Zone Generation in Electromagnetic Stirring[J].Transactions of the Iron and Steel Institute of Japan,1988(28):939. |
| [8] | 韩至成.电磁冶金技术及装备[M].北京:冶金工业出版社,2008 |
| [9] | 周尧和;胡壮麒;介万奇.凝固技术[M].北京:机械工业出版社,1998 |
| [10] | 张伟强.金属电磁凝固原理与技术[M].北京:冶金工业出版社,2004 |
| [11] | 王钦娟 .电磁离心铸造高速钢轧辊组织及性能研究[D].长安大学,2010. |
| [12] | 张西鹏,寇国军,吴春京.高碳高速钢的变质处理[J].铸造技术,2007(03):334-336. |
| [13] | 刘海峰,刘耀辉,于思荣.高碳高钒系高速钢的耐磨性研究[J].摩擦学学报,2000(06):401-406. |
| [14] | 徐流杰,魏世忠,张永振,邢建东,龙锐.轧辊用高钒高速钢的滚-滑动磨损性能及失效行为研究[J].摩擦学学报,2009(01):55-60. |
| [15] | 杜忠泽,符寒光,丰振军,李萍,戴建方.回火处理对铸造高速钢轧辊耐磨性的影响[J].材料热处理学报,2011(02):93-99. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%