采用粉末层铺法和无压烧结工艺制备了组元分布指数p分别为0.1、0.3、0.7和1的4种Y2O3-W梯度材料,并进行了4种材料在600℃和400℃温差下的急冷淬火循环热震试验.结果表明:在600℃温差下,经2次循环热震后,4种材料均失效.在400℃温差下,经40次循环热震后,4种材料均未发生失效断裂.随着循环热震次数的增多,热裂纹的长度和密度也随之增加.Y2O3-W梯度材料的抗热震性能随着组元分布指数p的增大逐渐增强.当组元分布指数p=1时,Y2O3-W梯度材料具有最好的抗热震性能.
参考文献
| [1] | Tetsui T..Development of a TiAl turbocharger for passenger vehicles[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20020(0):582-588. |
| [2] | Cui, R.J.;Tang, X.X.;Gao, M.;Zhang, H.;Gong, S.K..Microstructure and composition of cast Ti-47Al-2Cr-2Nb alloys produced by yttria crucibles[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2012:14-21. |
| [3] | B.P. Bewlay;M.R. Jackson;J.-C. Zhao;P. R. Subramanian;M.G. Mendiratta;J.J. Lewandowski.Ultrahigh-Temperature Nb-Silicide-Based Composites[J].MRS bulletin,20039(9):646-653. |
| [4] | 马国印.镍和镍合金耐腐蚀性分析[J].化工装备技术,2007(01):71-74. |
| [5] | 张显;成来飞;张立同;徐永东.铀及铀合金熔体与石墨坩埚涂层反应的热力学分析[J].稀有金属材料与工程,2003(3):187-190. |
| [6] | 谈军;周张健;钟铭;骆学广;屈丹丹.氧化钇弥散强化钨基复合材料的制备及其性能评价[J].中国钨业,2012(1):40-43. |
| [7] | Qian-Gang Fu;He-Jun Li;Ke-Zhi Li.Study on the thermal fatigue behavior of SiC coated carbon/carbon composites[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20061/2(1/2):335-338. |
| [8] | 苏哲安;杨鑫;黄启忠;黄伯云;柴立元;陈鸿亮.高温热震对具有SiC涂层的C/C复合材料压缩性能的影响[J].粉末冶金材料科学与工程,2012(1):102-108. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%