通过光学显微金相分析、XRD分析以及显微硬度测试等实验手段，研究Pt添加量为5%~60%的铸态Ni-Pt二元合金的显微组织与力学性能。实验结果表明，Pt质量分数在5%~60%的Ni-Pt二元合金铸态组织为NiPt单相固溶体，且Ni-Pt固溶体为置换型固溶体，其固溶强化主要由Pt原子固溶到Ni基体中产生晶格畸变所导致，各晶面间距d随铂质量分数呈线性增大的趋势，显微硬度随Pt质量分数的增加而增大，且满足：Hv=2.10×Pt%+85.04的线性数学表达式；铸态组织的柱状晶区的柱状晶随铂质量分数的增加向等轴晶和树枝晶发展，晶粒尺寸得到细化。当Pt质量分数达到6%时，铸态组织表现为发达的树枝晶，存在铸造裂纹。
The microstructure and mechanical properties of as-cast Ni-Pt binary alloys were studied by optical microscopy, X-ray diffraction(XRD) quantitative and qualitative analysis, micro-hardness testing. The results showed that Ni -Pt binary alloy is composed of NiPt single phase solid solution, the solid solution is substitutional solutes. Solid solution strengthening effect is caused by lattice distortion which induced by Pt atoms dissolve into Ni lattices. Each of interplanar spacing d is a linear increasing trend with the content of Pt. And also, the micro-hardness of the alloy increases when Pt content raises, which meets the following mathematical expressions:Hv=2.10×Pt%+85.04. Columnar crystal of as-cast organization changes into isometric and dendrites with the increase of the content of platinum and the grain size is refined. When the mass fraction of Pt reaches 60%, the as-cast organization is characterized by plentiful dendrites, and there are the casting cracks.
参考文献
| [1] | Sarkar J.Ferromagnetic sputtering targets and thin films for silicides and data storage[A].William Andrew Publishing,2014:501-565. |
| [2] | Utlu G;Artun?N .The calculation of the reflection coefficients by analyzing resistivity data of the Ni-Si silicide films formed at 850℃ by RTA[J].Microelectronic Engineering,2014,113:86-92. |
| [3] | B. A. Greenberg;N. A. Kruglikov;L. A. Rodionova .Optimised Mechanical Properties of Ordered Noble Metal Alloys[J].Platinum Metals Review,2003(2):46-58. |
| [4] | Gong W;Zhang L;Yao D et al.Diffusivities and atomic mobilities in fcc Ni-Pt alloys[J].Calphad-computer Coupling of Phase Diagrams & Thermochemistry,2009,61(1):100-103. |
| [5] | Danielewski M;Grzesik Z;Mrowec S .On the oxidation mechanism of Ni-Pt alloys at high temperatures[J].Corrosion Science,2011,53:2785-2792. |
| [6] | 胡赓祥.材料科学基础[M].上海:上海交通大学出版社,2010 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%