通过高速电喷镀工艺在Ni基高温合金K17表面沉积了纳米Zr02/Ni复合镀层,测定了K17合金和纳米ZrO2/Ni复合镀层在1000℃的氧化动力学曲线,采用SEM、XRD和显微硬度计分析了纳米ZrO2/Ni复合镀层的组织结构、表面形貌和表面显微硬度;实验结果表明,镀层中纳米ZrO2 的存在有利于细化复合镀层晶粒,提高复合镀层显微硬度;1000℃氧化5h后,纳米ZrO2/Ni复合镀层氧化膜由NiO,ZrO2和CrO2组成,1000℃氧化100h后,纳米ZrO2/Ni复合镀层氧化膜由NiO,NiCr2O4,ZrO2 and Cr2O3组成;纳米Zr02/Ni复合镀层中ZrO2和crO3的存在明显改善了K17合金的抗高温氧化性.
参考文献
| [1] | Ilia Valov;Dimitar Stoychev;Ts. Marinova .Study of the kinetics of processes during electrochemical deposition of zirconia from nonaqueous electrolytes[J].Electrochimica Acta,2002(28):4419-4431. |
| [2] | Mishra S B;Chandra K;Prakash S .Characterisation and erosion behaviour of NiCrAlY coating produced by plasma sprayed method on two different Ni-based superalloys[J].Materials Letters,2008,62:1999-2002. |
| [3] | Arnd Jung;Alexander Schnell .Crack growth in a coated gas turbine superalloy under thermo-mechanical fatigue[J].International Journal of Fatigue,2008(2):286-291. |
| [4] | Thery PY;Poulain M;Dupeux M;Braccini M .Adhesion energy of a YPSZ EB-PVD layer in two thermal barrier coating systems[J].Surface & Coatings Technology,2007(4/7):648-652. |
| [5] | Marion Bartsch;Bernd Baufeld;S. Dalkilic;L. Chernova;Michael Heinzelmann .Fatigue cracks in a thermal barrier coating system on a superalloy in multiaxial thermomechanical testing[J].International Journal of Fatigue,2008(2):211-218. |
| [6] | 王伟,钱士强,周细应,林文松.高速电喷镀纳米复合镀层组织与性能研究[J].材料热处理学报,2007(z1):243-248. |
| [7] | 王伟,钱士强,周细应,林文松,何庆如.高速电喷镀纳米聚四氟乙烯（PTFE）复合镀层的研究动态与展望[J].金属热处理,2006(04):1-4. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%