研究了超塑性变形过程中TC4钛合金激光焊接接头各区域显微组织演变规律,并对相关参数进行表征.结果表明,随着超塑性变形的进行,接头内针状马氏体组织发生α’→α+β相变,同时针状组织长大为片层,接头各区域显微组织逐渐均匀化,促进超塑性变形的进行；随着变形的进行,等轴化率逐渐升高；随着变形温度的升高或初始应变速率的降低等轴化率逐渐上升,促进焊缝超塑性变形的进行.提出采用平均晶粒尺寸来表征热影响区组织的转变程度.随着变形的进行,平均晶粒尺寸逐渐增大,随变形温度的升高或初始应变速率的降低平均晶粒尺寸减小,这有利于接头组织的均匀化.
参考文献
| [1] | Huang JC;Chuang TH .Progress on superplasticity and superplastic forming in Taiwan during 1987-1997[J].Materials Chemistry and Physics,1999(3):195-206. |
| [2] | Han Wenbo;Zhang Kaifeng;Wang Guofeng .Superplastic forming and diffusion bonding for honeycomb structure of Ti-6Al-4V alloy[J].Journal of Materials Processing Technology,2007(2/3):450-454. |
| [3] | Will J D;Kistner M G;Cotton J D .[P].US Patent PCL,1996. |
| [4] | Saresh N;Gopalakrishna Pillai M;Mathew Jose .[J].Journal of Materials Processing Technology,2007,192-193(01):83. |
| [5] | Zhang K F;Wang G F;Wu D Z .[J].Transactions of Nonferrous Metals Society of China,2002,12(02):251. |
| [6] | Will J D;Kistner M G;Cotton J D.[J].Superplasticity and Superplastic Forming,1998(02):321. |
| [7] | 郭鸿镇,张维,赵张龙,姚泽坤,虢迎光,王保善,赵永庆,曲恒磊.TC21新型钛合金的超塑性拉伸行为及组织演化[J].稀有金属材料与工程,2005(12):1935-1939. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%