采用固-固化学法,控制适当的工艺条件,制备了纳米级氧化锆及掺杂氧化锆粉体.经XRD,TEM和HRTEM表征,证明了产物大小均匀,形状规整,呈球状,分散性好,颗粒的平均粒径小于15nm.本论文研究了固-固反应过程中球磨的作用,在球磨机械力的作用下,扩散系数和局部反应温度升高,有利于反应的进行.对固-固化学法制备前驱物进行了热力学分析,证明了在低温球磨过程中固-固化学反应能够自发进行.
参考文献
| [1] | Nakatou M;Miura N .Detection of propene by using new-type impedancemetric zirconia-based sensor attached with oxide sensing-electrode[J].Sensors and Actuators, B. Chemical,2006(1):57-62. |
| [2] | D.Tibiletti;F.C.Meunier;A.Goguet .An investigation of possible mechanisms for the water-gas shift reaction over a ZrO_2-supported Pt catalyst[J].Journal of Catalysis,2006(2):183-191. |
| [3] | Amelinckx L;Kamrunnahar M;Chou P et al.Figure of merit for the quality of ZrO2 coatings on stainless steel and nickel-based alloy surfaces[J].Corrosion Science,2006,48(11):3646-3667. |
| [4] | 杨传铮;谢达材;陈癸尊.物相衍射分析[M].北京:冶金工业出版社,1989:195-200. |
| [5] | 陆家和;陈长彦.现代分析技术[M].北京:清华大学出版社,1995:81-89. |
| [6] | 曾锋 .超细ZrO2中锆的测定[J].景德镇陶瓷学院学报,1995,16(01):55-58. |
| [7] | GB/T 9286-1998.GB/T 9286-1998.氧化锆,氧化铪中氧化锆和氧化铪含量的测定(苦杏仁酸重量法)[S]. |
| [8] | Bochenok X H;荆家海;丁钏荣.Analytic Methods for Plant Biochemistry[M].北京:科学出版社,1981:111-112. |
| [9] | 元素周期表[OL].http://rsh.nst.pku.edu.cn/element/,2003-03-28. |
| [10] | Dean J A.Lange′s Handbook of Chemistry[M].United States of America:R.R.Donnelley & Sons Company,1999:682-6123. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%