分类综述了本征型抗静电涂料和复合型抗静电涂料的研究进展,详细介绍了碳系导电填料、金属导电填料和金属氧化物导电填料对抗静电涂料性能的影响.重点分析了抗静电涂料在雷达罩抗静电和石油罐导静电2个领域的应用现状及其在应用中存在的问题.探讨了抗静电涂料未来的发展方向,指出抗静电涂料的多功能化是未来的发展方向之一.
参考文献
| [1] | 史政海;张群安.浅色复合导电涂料[J].中国涂料,2004(7):30-32. |
| [2] | 王娜;程克奇;吴航;王福会.导电聚苯胺/水性环氧树脂防腐涂料的制备及防腐性能[J].材料研究学报,2013(4):432-438. |
| [3] | 易波;王群;郭红霞.聚苯胺/环氧树脂防静电涂料的研制[J].化工新型材料,2010(6):112-114. |
| [4] | Chang-Jian Weng;Ya-Lun Chen;Yu-Sian Jhuo.Advanced antistatic/anticorrosion coatings prepared from polystyrene composites incorporating dodecylbenzenesulfonic acid-doped SiO2@polyaniline core-shell microspheres[J].Polymer international,20135(5):774-782. |
| [5] | Luong, N.D.;Korhonen, J.T.;Soininen, A.J.;Ruokolainen, J.;Johansson, L.-S.;Sepp?l?, J..Processable polyaniline suspensions through in situ polymerization onto nanocellulose[J].European Polymer Journal,20132(2):335-344. |
| [6] | Stempien, Z.;Rybicki, T.;Rybicki, E.;Kozanecki, M.;Szynkowska, M. I..In-situ deposition of polyaniline and polypyrrole electroconductive layers on textile surfaces by the reactive ink-jet printing technique[J].Synthetic Metals,2015:49-62. |
| [7] | Sangermano, M.;Foix, D.;Kortaberria, G.;Messori, M..Multifunctional antistatic and scratch resistant UV-cured acrylic coatings[J].Progress in Organic Coatings: An International Review Journal,20139(9):1191-1196. |
| [8] | A. Roessler;H. Schottenberger.Antistatic coatings for wood-floorings by imidazolium salt-based ionic liquids[J].Progress in Organic Coatings: An International Review Journal,20143(3):579-582. |
| [9] | 李留东;董存峰;杨茂伟;狄志刚;付敏.抗静电涂料的抗静电机理探讨[J].涂料技术与文摘,2010(11):38-40,44. |
| [10] | 杨超;王云普;郭金山;刘汉功;李成林;高祥虎.膨胀石墨/叔氟乳液复合导电涂料的研究[J].现代涂料与涂装,2008(5):12-14. |
| [11] | 莫斌;刘祥萱;吴友朋;谢拯.炭黑/碳化硅复合导电涂料的制备及导电性能研究[J].现代涂料与涂装,2009(8):10-12. |
| [12] | 汪卫东;徐青;周双喜;邓文武.水性石墨电磁屏蔽导电涂料的制备及性能研究[J].材料导报,2013(z1):29-32. |
| [13] | 章勇 .石墨烯的制备与改性及在抗静电涂层中的应用[D].华东理工大学,2013. |
| [14] | 欧育湘;赵毅;许冬梅.聚合物/碳纳米管纳米复合材料性能研究进展[J].高分子材料科学与工程,2011(3):167-170. |
| [15] | 范凌云;蔡永明;沈晓冬;崔升;袁林生.丙烯酸酯/碳纳米管导电涂料的制备及其性能研究[J].材料开发与应用,2006(2):5-8. |
| [16] | 冯辉昌;王静;徐杰;张威震;孙继亮.储油罐纳米碳管导静电防腐涂料的研制[J].中国涂料,2006(11):24-26,38. |
| [17] | Rui Xie;Jiaping Wang;Yang Yang;Kaili Jiang;Qunqing Li;Shoushan Fan.Aligned carbon nanotube coating on polyethylene surface formed by microwave radiation[J].Composites science and technology,20111(1):85-90. |
| [18] | 刘栗加;周雪松;周郁文.铜金粉电磁屏蔽导电涂料[J].材料保护,2009(9):57-58. |
| [19] | 罗重霄;王燕;刘金库;连加松;柴春芳.导电ZAO纳米晶的超声-模板法合成、表征及应用[J].物理化学学报,2008(6):1007-1011. |
| [20] | 王书媚;税安泽;曾令可.氧化锌基复合抗静电涂层的制备[J].陶瓷,2009(5):17-20. |
| [21] | Zhiming Sun;Zhiqiang Bai;Hongling Shen;Shuilin Zheng;Ray L. Frost.Electrical property and characterization of nano-SnO2/wollastonite composite materials[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,20133(3):1013-1019. |
| [22] | Della Gaspera, E.;Bersani, M.;Cittadini, M.;Guglielmi, M.;Pagani, D.;Noriega, R.;Mehra, S.;Salleo, A.;Martucci, A..Low-temperature processed Ga-doped ZnO coatings from colloidal inks[J].Journal of the American Chemical Society,20139(9):3439-3448. |
| [23] | 王洪玮;狄志刚;付敏;袁立新;朱晓丰;刘宝成.新型飞机雷达罩弹性抗静电涂料施工工艺研究[J].涂料技术与文摘,2007(9):11-12,21. |
| [24] | 姜卫丽;刘华荣.雷达罩用新型抗静电防腐耐磨涂料的研制[J].现代涂料与涂装,2011(4):34-37. |
| [25] | 李旭东;范金娟.雷达罩抗静电涂层失效模拟[J].失效分析与预防,2009(3):133-137. |
| [26] | Jinjuan Fan;Chunhu Tao;Tao Jiang.Failure analysis on antistatic coatings on radome[J].Engineering failure analysis,2013:618-624. |
| [27] | 宋广成.石油罐导静电涂料概述[J].现代涂料与涂装,2010(10):16-19. |
| [28] | 宋广成;刘建卡.无溶剂环氧导静电防腐涂料的研制及性能测试（I）[J].现代涂料与涂装,2010(3):15-18. |
| [29] | 宋广成;刘建卡.无溶剂环氧导静电防腐涂料的研制及性能测试（Ⅱ）[J].现代涂料与涂装,2010(4):10-13,26. |
| [30] | 朱宇光.持久型耐油导静电聚氨酯弹性涂料的研究[J].现代涂料与涂装,2010(12):12-13,17. |
| [31] | 黄迎红;王亚雄.掺杂碳纳米管复合导电云母粉的制备[J].涂料工业,2009(6):10-13. |
| [32] | 喻冬秀;陈明涛;皮丕辉;文秀芳;程江;杨卓如.聚苯胺包覆短碳纤维的制备及电磁性能研究[J].高校化学工程学报,2009(1):148-153. |
| [33] | ZHANG Shan;WANG Cheng-guo;YUAN Hua;ZHU Bo;YU Mei-jie;ZHANG Bing-ming;HAN Rong-heng.Surface resistivity of carbonaceous fiber/PTFE antistatic coatings[J].中南大学学报（英文版）,2014(05):1689-1695. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%