Inclusion characteristic and microstructure of rare earth (RE) elements containing steel were evaluated with scanning electron microscopy with energy dispersive spectroscopy (SEM-EDS),element-mapping,optical microscopy (OM),and automated feature analysis (AFA) option equipped with ASPEX PSEM.Factsage was used tocalculate the equilibrium inclusion composition.Based on the calculation,an inclusion evolution mechanism was proposed.Furthermore,line scanning analysis was used to elucidate the intra-granular acicular ferrite (IAF) nucleation mechanism.The result showed that two different inclusions exist in sample steel:(Mn-Al-Si-Ti-La-Ce-O)+MnS complex inclusion and isolated MnS inclusion.Almost all nucleation sites for IAF are complex inclusions,while single MnS inclusion cannot induce IAF.A possible formation mechanism of complex inclusion is proposed based on calculated results using Factsage,which agrees well with experimental results.A Mn-depletion zone (MDZ) which exists adjacent to the (Mn-A1-Si-Ti-La-Ce-O) +-MnS complex inclusion can account for the IAF formation.However,the low volume fraction (1.49× 10-7)of effective inclusion may result in onlv 10％ (volume fraction) IAF.
参考文献
| [1] | J.M.GREGG;H.D.H.BHADESHIA .SOLID-STATE NUCLEATION OF ACICULAR FERRITE ON MINERALS ADDED TO MOLTEN STEEL[J].Acta materialia,1997(2):739-748. |
| [2] | D. S. SARMA;A. V. KARASEV;P. G. JONSSON .On the Role of Non-metallic Inclusions in the Nucleation of Acicular Ferrite in Steels[J].ISIJ International,2009(7):1063-1074. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%