采用射频磁控溅射法在室温、500℃的单晶硅和GCr15钢基体上制备了MoS2/SiC双层薄膜,并借助X射线衍射仪、扫描电子显微镜、摩擦磨损试验机以及划痕仪等研究了薄膜的结构、形貌、成分、摩擦学性能以及薄膜与基体的结合力。结果表明：当衬底温度为500℃时制备的MoS2/SiC双层薄膜表面致密平整,两层薄膜之间界面平直,膜厚约为0.8μm;该双层膜的摩擦因数低,耐磨性好;添加中间层可提高薄膜与基体的结合力。
The MoS2/SiC double films were prepared on single crystal silicon and GCr15 steel substrate,which temperature was room temperature and 500 ℃,by radio frequency magnetron sputtering method.The structure,morphology,components,tribological properties of the films and cohesion between film and substrate were studied by X-ray diffraction,scanning electron microscopy,friction and wear tester and scratch tester,respectively.The results show that the surface of MoS2/SiC double film prepared at substrate temperature of 500 ℃ was compact and flat,and the interface of two layer films was straight.The film exhibited excellent wear resistance and low friction coefficient.Adding interlayers could improve the cohesion between substrate and MoS2/SiC film.
参考文献
| [1] | 赵斌.金属弹簧片的二硫化钼喷涂[J].内燃机配件,2005(01):21-23. |
| [2] | 陈玮,张晔.MoS2基复合润滑薄膜的制备及其摩擦性能[J].机械工程材料,2008(08):47-49. |
| [3] | Ding, X.-Z.;Zeng, X.T.;He, X.Y.;Chen, Z. .Tribological properties of Cr- and Ti-doped MoS_2 composite coatings under different humidity atmosphere[J].Surface & Coatings Technology,2010(1):224-231. |
| [4] | Cardinal, MF;Castro, PA;Baxi, J;Liang, H;Williams, FJ .Characterization and frictional behavior of nanostructured Ni-W-MoS2 composite coatings[J].Surface & Coatings Technology,2009(1/2):85-90. |
| [5] | 宋文龙,邓建新,张辉.MoS2-Zr复合薄膜的摩擦磨损特性研究[J].润滑与密封,2008(02):35-39. |
| [6] | 李亚平,安霞,薛成山.碳化硅薄膜生长技术的研究进展[J].山东师范大学学报（自然科学版）,2004(02):37-40. |
| [7] | Naka M;Feng JC;Schuster JC .Phase stability of SiC against Ti at high temperature[J].Vacuum: Technology Applications & Ion Physics: The International Journal & Abstracting Service for Vacuum Science & Technology,2008(1):223-225. |
| [8] | 张建军,刘文安.SiC/Fe/SiC连接件高温温度场分布的计算[J].新技术新工艺,2009(06):114-115. |
| [9] | Liu YS;Cheng LF;Zhang LT;Wu SJ;Li D;Xu YD .Oxidation protection of multilayer CVD SiC/B/SiC coatings for 3D C/SiC composite[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1-2):172-177. |
| [10] | 冉丽萍,易茂中,蒋建献,葛毅成.炭/炭复合材料MoSi2/SiC高温抗氧化复合涂层的制备及其结构[J].新型炭材料,2006(03):231-236. |
| [11] | 黄敏,李克智,李贺军,付前刚,王字,许天旱.包埋工艺参数对碳/碳复合材料表面SiC涂层致密性的影响[J].机械工程材料,2009(03):5-7,11. |
| [12] | 王剑屏,郝跃,彭军,朱作云,张永华.碳化硅异质外延薄膜生长及表面缺陷研究[J].西安电子科技大学学报(自然科学版),2002(04):465-469. |
| [13] | 邵红红,陈威.射频磁控溅射法制备二硫化钼薄膜[J].润滑与密封,2007(12):43-46. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%