采用高速压制技术制备铁基制品, 探讨了冲击能量及冲击速度与冲击行程之间的关系, 并研究了冲击能量、压制方式对生坯密度、最大冲击力、脱模力和径向弹性后效的影响. 结果表明: 在高速压制过程中, 冲击能量与冲击行程呈线性关系,而冲击速度与冲击行程呈抛物线关系. 生坯密度随着冲击能量的增加而逐渐增大.单次压制时, 当冲击能量增加到 6510 J时, 生坯密度达到7.336 g/cm3,其相对密度约为97%. 在总冲击能量相同的情况下, 两次压制制备出的试样生坯密度最大,三次压制的最小. 在高速压制过程中, 试样的脱模力及其径向弹性后效均远低于传统压制.
Ferrous parts were prepared through high velocity compaction (HVC), the relationship between the impact energy, the impact velocity and the stroke length was investigated. The effects of impact energy and compaction methods on the green density, the maximal impact force, the withdraw force and the radial springback were discussed. The results showed that the impact energy was direct proportional to the stroke length and the impact velocity is parabolic to it. The green density increased with the impact energy increasing. In single impact the green density was 7.336 g/cm3, relative density about 97%, when impact energy was 6510 J. For the same total impact energy the green density of specimen processed by double impacts was the best and that of specimen fabricated by triplex impacts was the lowest. The withdraw force and the radial springback of specimen produced by HVC were all lower than that of specimen processed by traditional compaction.
参考文献
| [1] | |
| [2] | |
| [3] | |
| [4] | |
| [5] | |
| [6] | |
| [7] |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%