对镀锌层上墨绿色钝化膜进行了扫描电子显微镜(SEM)和x射线光电子能谱(XPS)分析.SEM观察表明,钝化膜表面较为均匀平整,钝化膜层与镀锌层之间以及镀锌层与钢铁基体之间均结合紧密,没有裂纹等组织缺陷出现,镀锌层及钝化膜层较厚,共12.423μm,其中墨绿色钝化膜层厚度为1.734 μm.XPS分析结果表明,钝化膜由Cr、O、P、N、Zn等元素组成,并可能以CrOOH、Cr(OH)3、Cr2O3、ZnO、Zn3(PO4)2·4H2O、FeOOH、Fe(OH)3、Cr2(SO4)3等化合物的形式存在于钝化膜中.经墨绿色钝化工艺处理的环保锌覆层钢板,外观呈墨绿色,色泽均匀,光度柔和,满足了客户要求.
参考文献
| [1] | Baghni IM;Lyon SB;Ding BF .The effect of strontium and chromate ions on the inhibition of zinc[J].Surface & Coatings Technology,2004(2/3):194-198. |
| [2] | ARAMAKI K .Self-healing mechanism of an organosiloxane polymer film containing sodium silicate and cerium(Ⅲ)mitrate for corrosion of scratched zinc surface in 0.5 M NaCl[J].Corrosion Science,2002,44(07):1621-1632. |
| [3] | A. B. Velichenko;M. Sarret;C. Muller .Nature of the passive film formed at a zinc anode in zinc-nickel containing solutions[J].Journal of Electroanalytical Chemistry: An International Journal Devoted to All Aspects of Electrode Kinetics, Interfacial Structure, Properties of Electrolytes, Colloid and Biological Electrochemistry,1998(1):1-3. |
| [4] | VITKOVA S;NIKOLOVA M;IVANOVA V et al.Composition of passive chromate films on a Zn-Sn alloy[J].Surface and Coatings Technology,1996,82(03):239-246. |
| [5] | 陈培榕;李景虹;邓勃.现代仪器分析实验与技术[M].北京:清华大学出版社,1999:308-321. |
| [6] | 李克安.分析化学教程[M].北京:北京大学出版社,2005:473-496. |
| [7] | 祁景玉.现代分析测试技术[M].上海:同济大学出版社,2006:1-174. |
| [8] | 王鸿建.电镀工艺学[M].哈尔滨:哈尔滨工业大学出版社,1988:91. |
| [9] | 刘新锦;朱亚先;高飞.无机元素化学[M].北京:科学出版社,2005:261. |
| [10] | 王宏.镀锌钢板墨绿色钝化膜的腐蚀行为[J].电镀与涂饰,2009(11):29-30,32. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%