用聚乙烯醇缩丁醛(PVB)作为本体高分子材料,用浸没沉淀相转化法制备PVB不对称超滤膜;扫描电镜照片显示所制膜的超滤结构.研究了PVB本体浓度、制膜间隙、凝胶浴温度以及乙酸添加剂等因素对PVB不对称超滤膜性能的影响;比较了乙酸及聚乙烯基吡咯烷酮(PVP)作为添加剂对大孔径PVB超滤膜皮层结构的影响.当PVB本体浓度为12%时,膜的纯水通量及牛血清白蛋白(BSA)溶液通量分别为876.4 L/(m2·h)和89.8 L/(m2·h),此时膜对BSA的截留率为96.8%;PVB膜纯水通量随着制膜间隙的增加及凝胶浴温度的上升而降低;乙酸及PVP的添加均提高了PVB超滤膜的纯水通量,通量增加幅度分别为136%和171%.
参考文献
| [1] | Choi JG.;Bae TH.;Kim JH.;Tak TM.;Randall AA. .The behavior of membrane fouling initiation on the crossflow membrane bioreactor system[J].Journal of Membrane Science,2002(1/2):103-113. |
| [2] | Cho BD.;Fane AG. .Fouling transients in nominally sub-critical flux operation of a membrane bioreactor[J].Journal of Membrane Science,2002(2):391-403. |
| [3] | Jefferson B;Laine A L;Judd S J et al.Membrane bioreactors and their role in wastewater teuse[J].Water Science and Technology,2000,41(01):197-204. |
| [4] | Wagner J.;Rosenwinkel KH. .Sludge production in membrane bioreactors under different conditions[J].Water Science and Technology,2000(10/11):251-258. |
| [5] | 钱知勉.塑料性能应用手册[M].上海:上海科学技术文献出版社,1982:106-116. |
| [6] | Denizli A.;Salih B.;Aydinlar E.;Ozdural A.;Piskin E.;Tanyolac D. .ADSORPTION OF HEAVY-METAL IONS ON CIBACRON BLUE F3GA-IMMOBILIZED MICROPOROUS POLYVINYLBUTYRAL-BASED AFFINITY MEMBRANES[J].Journal of Membrane Science,1997(1/2):1-8. |
| [7] | Gotoh M;Tamiya E;Karube I .Polyvinylbutyral resin membrane for enzyme immobilization to an inset microbiosensor[J].Journal of Molecular Catalysis,1986,37:133-141. |
| [8] | Mulder M;李琳.膜技术基本原理[M].北京:清华大学出版社,1999:92-94. |
| [9] | 李书申;吴开芬;韩式荆 .大孔径聚砜超滤膜的研究[J].环境化学,1993,12(06):464-468. |
| [10] | 张耀鹏,邵惠丽,沈新元,胡学超.凝固浴和铸膜液对新型纤维素超滤膜的影响[J].中国纺织大学学报,2000(04):90-92. |
| [11] | 何昌生,孙雪雁.小孔径磺化聚砜超滤膜研制[J].水处理技术,1998(05):265. |
| [12] | 陈忠祥,周美娟,肖通虎,陈珊妹.非溶剂草酸对形成聚醚砜微孔膜的影响研究[J].膜科学与技术,2001(06):21-26. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%