采用自行研制的装置,对不锈钢加强Bi-2223/Ag高温超导带材的焊接工艺进行了系统研究,得出最佳的焊接方案.实验测量高温超导带材焊接头的直流电阻,并对带材进行了交流过电流冲击实验,冲击时间为0.5秒,每次冲击的电流依次递增,并在每次冲击后测量焊接头的电阻,直到被测带材烧毁.根据实验数据对样品在过流冲击下的动态电阻进行实验研究,得到了具有实际意义的结果.
参考文献
| [1] | Tsutomu Hoshino;Itsuya Muta .[J].IEEE Transactions on Applied Superconductivity,1994,30:2018-2021. |
| [2] | P Mehta .Nicola Aversa and Michaels[J].Walker IEEE Spectrum,1997,34:43-49. |
| [3] | K. Ryu;S. W. Kim;B. J. Choi;S. D. Hwang .Fault Current Characteristics in a Technical High T{sub}c Superconductor[J].IEEE Transactions on Applied Superconductivity,2004(2):658-661. |
| [4] | Yukikazu Lwasa.Case Studies in Superconducting Magnets,A Division of Plenum Publishing Corporation[M].New York:Plenum Press,1994 |
| [5] | Luc Le Lay;Darren M. Spiller;Olivier Belmont .Over critical-current behaviour of Bi-2223 tapes[J].IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee,1999(2 Pt.1):1324-1327. |
| [6] | Y Iwasa;E J EcNiff;R H Bellis;K Sato .[J].Cryogenics,1993,33:836-837. |
| [7] | 张国民,林良真,肖立业,丘明,舒立,余运佳.传输交流的Bi2223/Ag高温超导带在不同取向交流外场下的交流损耗[J].低温物理学报,2002(01):23-29. |
| [8] | 王银顺,肖立业,林良真,戴少涛,舒立.银包套Bi2223多芯带材局部临界电流的变化对整个长样带材性能的影响[J].低温物理学报,2002(03):218-223. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%