Mesoporous TiO2-CeO2 mixed oxide(m-TiO2-CeO2) were synthesized using n-cetylpyridinium chloride (C16PyCl) as a structure-directing agent under the neutral conditions and room temperature. The synthesized mesoporous samples were characterized by FT-IR, XRD, and N2 adsorption BET methods. The incorporation of Ce3+ ions into the channel wall improves the stability of the mesoporous structure obviously. After ruthenium being loaded by the impregnating method, the Ru particle strongly interacts with the mesoporous mixed supports. Although a part of the particles are possible to block the support pores, the catalytic activity of ruthenium supported on the m-TiO2-CeO2 for methanol decomposition to carbon monoxide and hydrogen is significantly higher than that of ruthenium supported on m-TiO2. A synergistic effect between CeO2 and TiO2 was observed for promoting the catalytic properties of Ru.
参考文献
| [1] | Mahendra K P;Yuichi I;Koji K et al.Catalytic methanol decomposition over palladium deposited on thermally stable mesoporous titanium oxide[J].Journal of Molecular Catalysis A:Chemical,2003,198:303. |
| [2] | Usami Y;Kagawa K;Kawazoe M et al.Catalytic methanol decomposition at low temperatures over palladium supported on metal oxides[J].Applied Catalysis A:General,1998,171:123. |
| [3] | Antonelli D M .Synthesis of phosphorus-free mesoporous titania via templating with amine surfactants[J].Microporous and Mesoporous Materials,1999,30:315. |
| [4] | M.P.Kapoor;Anuj Raj;Yasuyuki Matsumura .Methanol decomposition over palladium supported mesoporous CeO_2-ZrO_2 mixed oxides[J].Microporous and Mesoporous Materials,2001(0):565-572. |
| [5] | Nishimura T;Omata T;Ogisu Y.Eco-Energy City System[M].Tokyo:Energy Conservation Center (in Japanese),1999:186. |
| [6] | Matsumura Y;Kuraoka K;Usami Y et al.Production of carbon monoxide and hydrogen by methanol decomposition over nickel dispersed on porous glass[J].Catalysis Today,1998,45:191. |
| [7] | Yang P;Zhao D;Margolese D I et al.Block copolymer templating syntheses of mesoporous metal oxides with large ordering lengths and semicrystalline framework[J].CHEMISTRY OF MATERIALS,1999,11:2813. |
| [8] | Fang X M;Li F Y;Zhou Q et al.Effect of heavy rare earth addition on properties of KL zeolite-supported platinum reforming catalyst[J].Applied Catalysis A:General,1997,161:227. |
| [9] | 罗来涛,李松军,邓庚凤.Study on Modification of Sm2O3 by Ni/Sepiolite Catalyst[J].稀土学报(英文版),2003(04):494-497. |
| [10] | Shi Q J;Li F Y;Luo L T et al.The studies on the modification of amorphous NiB alloy catalyst by light rare earth oxides[J].Journal of Molecular Catalysis(China),1999,13(01):9. |
| [11] | WANG Min-wei,LUO Lai-tao,LI Feng-yi,WANG Ji-jun.Effect of La2O3 on Methanation of CO and CO2 over Ni-Mo/γ-Al2O3 Catalyst[J].中国稀土学报（英文版）,2000(01):22-26. |
| [12] | Wang H M;Lu Q J;Zhou X K .Determination of surface of the Ni supported catalyst by pulsed chromatography[J].Chemistry-a European Journal,1981,1:31. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%