本文以气固反应硫化得到的γ-La2S3粉体为原料,采用热压烧结的方法制备出了γ-La2S3多晶体片.研究了不同Ca2+掺杂量对得到粉体相结构的影响,并分析了烧结温度、保温时间对多晶体γ-La2S3红外透过率的影响.结果表明:掺入碱土金属离子Ca2+有利于低温获得稳定的高温型γ-La2S3相,在Ca/La物质的量比为1:5～1:15时能得到纯相的γ-La2S3粉体.在烧结温度为1100 ℃,保温时间为1 h时制备出的γ-La2S3多晶体片,晶粒细小均匀,无明显气孔,在10～14 μm波段的最大红外透过率约为40%.
参考文献
| [1] | 周育先,方珍意,潘伟,杨曜源,张力强,王向阳,肖红涛.低压化学气相沉积法制备ZnSe多晶及其性能研究[J].稀有金属材料与工程,2005(02):306-308. |
| [2] | 黄占杰 .中红外导流罩及窗口材料的发展趋势[J].材料导报,1998,12(03):30-33. |
| [3] | Blodgett D W;Thomes M E;Itahn D V et al.Longwave Infrared Absorption Properties of ZnS and ZnSe[J].SPIE,2003,5078:137-147. |
| [4] | 杨曜源,李卫,张力强,蔡以超,王向阳,肖红涛,田鸿昌,东艳萍,方珍意,郝永亮.ZnS晶体的化学气相沉积生长[J].人工晶体学报,2004(01):92-95. |
| [5] | Lewis K L;Savage J A;Marsh K J .New Optical Materials[J].Spie,1983,400:21-28. |
| [6] | Kunita P N;Risbud S H .Review:Rare-earth Chalcogenides-an Emerging Class of Optical Materials[J].Materials Science,1994,29:1135-1158. |
| [7] | Tsay B J;Wang L H .A Study on Infrared Transmission of Lanthanum Sulfide and Oxysulfide in 2.5-14 μm Region[J].Materials Letters,1998,34:180-183. |
| [8] | Gentilman R L;Dekosky M B;Wong T Y et al.Calcium Lanthanum Sulfide as a Long Wavelength IR Materials[J].SPIE,1988,929:57-64. |
| [9] | Kumta P N;Risbud S H .Low Temperture Chemical Routes to Formation and IR Properties of Lanthanum Sesquisulfide(La2S3) Ceramics[J].Materials Research,1993,8(06):1394-1410. |
| [10] | Kamta P N;Risbudt S H .Chemical Process of Rare Earth Chalcogenides[J].Crystal Growth and Charact,1991,22:321-383. |
| [11] | Herdorson J R;Haramott H;Loh E .Electronic Structure of Rare-earth Sesquisulfide Crystals[J].Chemical Physics,1967,47(09):3347-3356. |
| [12] | Romero S.;Trombe JC.;Mosset A. .Study of some ternary and quaternary systems based on gamma-Ce2S3 using oxalate complexes: stabilization and coloration[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,1998(1/2):98-106. |
| [13] | Ming S Y;Yong M H .Fabrication of Calcium lanthanum Sulfide Ceramic by Carbonate Coprecipitaation Method[J].Scripta Metallurgica et Materialia,1995,32(05):713-718. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%