采用反应挤出的方式,首先对非极性的高密度聚乙烯进行功能化处理,得到HDPE-g-MAH,然后将其与有机蒙脱土熔融复合,制得了分散效果良好的纳米复合材料.并用红外对接枝效果进行验证,用XRD,TEM对复合体系的插层效果进行了分析和表征.进一步的热性能分析显示,纳米材料的热稳定性相对于纯聚乙烯有所提高;同时DSC 研究结果表明,复合体系的结晶温度也有所提高.
参考文献
| [1] | Shelley J S;Mather P T;Devries K L.[J].POLYMER,2001:5849-5858. |
| [2] | Agag T;Koga T;Takeichi T.[J].POLYMER,2001:3399-3408. |
| [3] | Xu WB.;Liang GD.;Zhai HB.;Tang SP.;Hang GP.;Pan WP. .Preparation and crystallization behaviour of PP/PP-g-MAH/Org-MMT nanocomposite[J].European Polymer Journal,2003(7):1467-1474. |
| [4] | Alexandre M.;Dubois P.;Sun T.;Garces JM.;Jerome R. .Polyethylene-layered silicate nanocomposites prepared by the polymerization-filling technique: synthesis and mechanical properties[J].Polymer: The International Journal for the Science and Technology of Polymers,2002(8):2123-2132. |
| [5] | Shin S Y A;Simon L C;Soares J B P.[J].POLYMER,2003:5317-5321. |
| [6] | Wang K H;Min Ho Choi M H;Koo C M.[J].POLYMER,2001:9819-9826. |
| [7] | Zhang J G;Charles A.[J].Polymer Degradation and Stability,2002:2123-2132. |
| [8] | Gopakumar T G;Lee J A;Kontopoulou M.[J].POLYMER,2002:5483-5491. |
| [9] | 徐卫兵;蔡琼英.[J].合肥工业大学学报(自然科学版),1992(zk):128-131. |
| [10] | 瞿金平;李光吉;周南桥.反应挤出-原理与实践[M].北京:化学工业出版社,1999:58. |
| [11] | Nam P H;Maiti P;Okamoto M.[J].POLYMER,2001:9633-9640. |
| [12] | Gilman J W .[J].Applied Clay Science,1999,15:31-49. |
| [13] | 张景春,谢续明,柯华.GMA/苯乙烯多组分单体接枝聚丙烯结晶行为研究[J].高分子学报,2002(01):13-18. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%