The oxidization resistance of the Ni76Cr19AlTi alloy was studied by a static oxidization experiment at 600-800 ℃. The results show that the oxidation behavior of the alloy can be explained by a kinetic equation:(△m/S)2= Kpt +C, where Kp is a kinetic constant of the nickel-base alloy.The higher the experimental temperature,the higher the value of Kp.It is discovered that the microstructure of the oxide scales is compact and the thickness of it is less than 10 μm.The oxidization of the alloy is in the first grade.It is also found that the oxide scales are mainly composed of Cr2O3 and TiO2.Chrome and titanium react more easily with oxygen at temperatures under the operating mode.
参考文献
| [1] | Kano M;Tanimoto I;Nakamura K;Fujiki A .Effects of the EGR system on valve train wear in diesel engine[J].JOURNAL OF JAPAN SOCIETY OF LUBRICATION ENGINEERS,1987,32(12):900. |
| [2] | Wang Y S;Narasimhan S;Larson J M;Larson J E .Effect of operating conditions on heavy duty engine valve seat wear[J].Wear,1996,201(1-2):15. |
| [3] | Ootani T;Yahata N;Fujiki A;Ehira A .Impact wear characteristics of engine valve and valve seat insert materials at high temperature[J].Wear,1995,188(1-2):175. |
| [4] | Zhao R;Barber G C;Wang Y S;Larson J E .Wear mechanism analysis of engine exhaust valve seats with a laboratory simulator[J].TRIBOLOGY TRANSACTIONS,1997,40(02):209. |
| [5] | Ootani T;Yahata N;Fujiki A;Ehira A .Impact wear characteristics of engine valve and valve seat insert materials at high temperature[J].JSME Int J Series C,1996,39(01):15. |
| [6] | 李云,尚海波,郭建亭,袁超,杨洪才.铸造镍基高温合金K35的高温氧化行为[J].金属学报,2003(07):749-754. |
| [7] | D. K. Das;Vakil Singh;S. V. Joshi .High temperature oxidation behaviour of directionally solidified nickel base superalloy CM-247LC[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2003(6):695-708. |
| [8] | Wang B;Lu C Y;Sun C .Effect of NiCrAlY coatings on oxidation resistance of Ni-base superalloy K17[J].Corros Sci Prot Technol,2002,14(01):7. |
| [9] | Li M H;Sun X F;Jin T;Hu Z Q .Oxidation behavior of a single-crystal Ni-base superalloy in air-Ⅱ:At 1000,1100,and 1150 degrees C[J].Oxidation of Metals,2003,60(1-2):195. |
| [10] | A. Anderko;N. Sridhar;L.T.Yang .Validation of localised corrosion model using real time corrosion monitoring in a chemical plant[J].Corrosion Engineering, Science and Technology,2005(1):33-42. |
| [11] | S. Mrowec;Z. Grzesik;B. Rajchel .Oxidation of Nickel and Ni-Cr and Ni-Na Alloys at High Temperatures[J].HIGH TEMPERATURE MATERIALS AND PROCESSES,2004(1):59-72. |
| [12] | K. Asami;H. M. Kimura;K. Hashimoto .High Temperature Oxidation Behavior of Amorphous Zr-Ni Alloys in Air[J].Materials Transactions, JIM,1995(7):988-994. |
| [13] | Iuchi T.;Furukawa T.;Wada SE. .Emissivity modeling of metals during the growth of oxide film and comparison of the model with experimental results[J].Applied optics,2003(13):2317-2326. |
| [14] | Lowell C E;Barrett C A;Palmer R W .A computer model of cyclic oxidation[J].Oxidation of Metals,1991,36(1-2):81. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%