介绍了致密Cr2 O3制品的组成及其作用、生产工艺流程及相应要点、制品的显微结构特征、性能指标和应用情况.着重论述了影响制品性能的成型和烧成工艺,表明了烧成气氛中的氧分压对致密Cr2O3制品的致密化程度有至关重要的作用,控制烧成气氛可以有效获得一定致密化程度的致密Cr2O3制品,而采用埋炭气氛烧成的致密Cr2O3制品,具有高度致密化结构.
参考文献
| [1] | Keiichi Nobuhara;Kensaku Matsuda .Refractories for glass fiber furnace[J].Taikabutsu Overseas,1986,6(04):13-17. |
| [2] | Evans G .Glassmaking refractories--looking to the future[J].Glass Technology,2005,41(04):109-111. |
| [3] | 尹洪基,耿可明,徐延庆.致密Cr2O3耐火材料及其应用[J].玻璃,2007(01):29-33. |
| [4] | McGarry C N;Monroe D L;Webber R A .New thermal shock-resistant dense zircon and dense chromic oxide refractories[J].Ceramic Engineering and Science Proceedings,1991,12(3-4):473-481. |
| [5] | Ownby P D;Jungquist G E .Final sintering of Cr2 O3[J].Journal of the American Ceramic Society,1972,55(09):433-436. |
| [6] | Callister W D;Johson M L;Cuder I B et al.Sintering chromium oxide with the aid of TiO2[J].Journal of the American Ceramic Society,1979,62(03):208-211. |
| [7] | 尹洪基,徐延庆,吕世坪,王金相.气氛对氧化铬材料烧结的影响[J].耐火材料,2010(04):251-255. |
| [8] | 尹洪基,耿可明,王金相.氧化钛对氧化铬材料烧结特性的影响[J].硅酸盐学报,2009(12):1995-1999. |
| [9] | Roy S N;Guha S K;Maiti H S.Studies on the influence of lanthanum oxide on the sinterability of chromium (Ⅲ)-oxide[J].Journal of Materials Science,1990:3508-3512. |
| [10] | 陆佩文.无机材料科学基础[M].武汉:武汉理工大学出版社,1 996:298-308. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%