以二级矾土熟料和特级焦宝石为主要原料,以电熔镁砂细粉和硅灰作结合剂,配制中间包永久衬浇注料.研究了电熔镁砂细粉和硅灰用量对MgO-SiO2-H2O结合浇注料物理性能的影响.结果表明:在硅灰和镁砂细粉的质量分数分别为4%时,该浇注料试样经110℃24h烘干和1100、1400℃保温3h热处理后的冷态耐压强度分别达99.0、138和156MPa,1100℃水冷热震3次后的抗折强度保持率为46%,耐压强度保持率为89%,上述性能均优于同材质低水泥结合高铝质浇注料的.
参考文献
| [1] | Li Nan;Wei Yaowu.Properties of MgO-SiO2 castable and effect of reactions in microsilica-MgO bond system[A].Berlin,Germany,1999:97-101. |
| [2] | 周宁生;张三华;陈志强 等.矾土基高铝-尖晶石质钢包浇注料的特性研究[J].耐火材料,1996,30(06):314-318. |
| [3] | Bjφrn Myhre.Cement-free castable in system MgO-SiO2,the effect of bond phase modifiers on strength[A].Cincinnati,Ohio,1991:78-84. |
| [4] | 表心愚 .铝镁浇注料在高温作业钢包中的应用[J].耐火物(日本）,1995,47(06):291-294. |
| [5] | Cunha F N,Bradt.Reactions of constituents for insitu bonds of MgAl2O4,Mg2SiO4 and 3Al2O3·2SiO2 in refractories[A].Pittsburgh,PA,USA,1999:143-152. |
| [6] | Swe-Kai Chen;Min-Yuan Cheng .Thermal character-istics of Al2O3MgO and Al2O3-spinel castables for steel ladles[J].Ceramics International,2002,28:811-817. |
| [7] | 魏耀武,李楠,吴宏鹏.硅微粉对MgO-SiO2-H2O系统中水合物形成的影响[J].耐火材料,2001(05):255-257. |
| [8] | 韦江雄,陈益民.常温下MgO-SiO2-H2O体系胶凝性的研究[J].武汉理工大学学报,2006(02):14-16,33. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%