研究了催化剂、原料品种、反应温度、硬段含量、R值等因素对聚醚型热塑性聚氨酯弹性体（TPU）合成的影响，并对产物力学性能进行了分析。结果表明：Bi-8、100-Ag与TPT三种催化剂的催化效果都随起始反应温度的升高而增强；随着硬段含量的提高，TPu的硬度、拉伸强度、定伸模量、撕裂强度都同步增大，断裂伸长率则减小；随着R值的增加，TPU的力学性能提高；同时，采用PTMEG-1000合成的TPU的综合性能比采用PTMEG-1800合成的要好；与路博润同硬度产品相比，采用PTMEG-1000合成的TPu在100％定伸模量、3009／6定伸模量和撕裂强度上有所提高，但断裂伸长率和拉伸强度表现稍差。
The effects of catalysts, materials ,reaction temperature, hard segment content and R value on the synthesis of polyether type thermoplastic polyurethane elastomer(TPU) and mechanical property of synthetic TPU were investigated. Results show catalytic effect of three of catalyst, Bi-8, 100-Ag and TPT, rose up when the initial reaction temperature increased. With the increase of hard segment content, the hardness, tensile strength, set out modulus, tear strength of PTMEG-1000 and PTMEG-1800 TPU improved, but breaking elongation decreased. With the increase of R value, mechanical properties of TPU improved. TPU synthesized using PTMECrl000 exhibited better the comprehensive property than that using PTMEG-1800. Compared with the product of Noveon, TPU synthesized using PTMGE-1000 had better mechanical property in 100% elongation, 300% elongation modulus and tear strength, but worse in breaking elongation and tensile strength.
参考文献
| [1] | 王瑶,赵志军,刘俊龙.聚氨酯弹性体的研究进展[J].橡塑技术与装备,2006(12):24-28. |
| [2] | 陈由亮 .聚氨酯弹性体耐热性能的研究[D].青岛科技大学,2009. |
| [3] | 苏丽丽,石雅琳,韦永继.TODI型热塑性聚氨酯弹性体的制备与性能研究[J].化学推进剂与高分子材料,2011(06):82-84,88. |
| [4] | 郑申声,关立峰,董兰,吴奎先.HTPB/N100体系的聚合反应动力学和粘度变化[J].含能材料,2011(03):291-294. |
| [5] | 张欢琴,白子文.TPU生产配方的设计与调整[J].聚氨酯工业,2005(04):38-41. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%