采用硼氢化钾液相一步法还原硫酸铜水溶液,加入了络合剂EDTA-2Na和阳离子型分散剂CTAB(C19H42NBr),获得了铜纳米流体.由动态光散射粒度分析仪测得加入0.05mol/L CTAB的纳米流体的平均粒度仅为1.02nm,经X射线衍射分析离心分离所得粉末绝大部分为纯净的纳米铜粉,还存在极少量的Cu2O,这受到络合剂EDTA-2Na化学反应的影响.
参考文献
| [1] | Choi S U S.Developments and Applications of Non-Newtonian Flows[M].New York,1995:99-105. |
| [2] | Jacques van Wonterghem;Steen Morup;Christian J W Koch et al.[J].NATURE,1986,322(14):622-623. |
| [3] | 黄钧声,任山,谢成文.化学还原法制备纳米铜粉的研究[J].材料科学与工程学报,2003(01):57-59. |
| [4] | Kuo P Lin;Liang W J;Wang F Y .[J].Colloid and Polymer Science,2006,284:435-442. |
| [5] | Hai-tao Zhu;Yu-sheng Lin;Yan-sheng Yin .A novel one-step chemical method for preparation of copper nanofluids[J].Journal of Colloid and Interface Science,2004(1):100-103. |
| [6] | Zhu Haitao;Zhang Canying;Yin Yansheng .[J].Journal of Crystal Growth,2004,270(3-4):722-728. |
| [7] | Ananda K S;Shree M K;Narashimhan B R V .[J].Materials Chemistry and Physics,2009,113(01):57-62. |
| [8] | Garg J;Poudel B;Chiesa M et al.[J].Journal of Applied Physics,2008,103(07):074301. |
| [9] | 李新芳,朱冬生,王先菊,汪南,李华,杨硕.Cu-水纳米流体的分散行为及导热性能研究[J].功能材料,2008(01):162-165,169. |
| [10] | Liu Minsheng;Lin Mark Ching-Cheng;Tsai C Y .[J].International Journal of Heat and Mass Transfer,2006,49:3028-3033. |
| [11] | 秦赢,张鹏远,陈建峰.液相还原法制备纳米铜粉[J].北京化工大学学报（自然科学版）,2006(06):86-88. |
| [12] | 高濂;孙静;刘阳桥.纳米粉体的分散及表面改性[M].北京:化学工业出版社,2003:149-150. |
| [13] | Li Xinfang;Zhu Dongsheng;Wang Xianju .[J].Journal of Colloid and Interface Science,2007,310:456-463. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%