采用金相显微镜、电子显微镜等手段研究控轧控冷工艺对Ti微合金化高强钢的组织和性能的影响.结果表明:在低温终轧(800℃)、600℃保温1h的试验钢的屈服强度和抗拉强度最高,分别为670.7 MPa和752 MPa.高温终轧(1 030℃)的试验钢组织主要为准多边形铁素体、针状铁素体和粒状贝氏体,组织粗大;低温终轧(800℃)的组织主要为多边形铁素体,晶粒较细小.在600℃保温1h的试验钢中存在大量的纳米尺寸TiC粒子,沉淀强化效果明显,未在600℃保温1h的试验钢中,TiC的析出受到限制,沉淀强化效果明显减弱.

The effects of controlled rolling and cooling process on the microstructure and properties of Ti micro-alloyed high strength steel were investigated by metalloscope,SEM and TEM,etc.The results show that the highest yield strength and tensile strength of the steel sample are respectively 670.7 MPa and 752 MPa at 800 ℃ of low temperature final rolling and 600 ℃ for 1 h of insulation.The steel sample at high rolling temperature (1 030 ℃) has coarse microstructures of quasi-polygonal ferrite,acicular ferrite and granular bainite,and the sample at low rolling temperature (800 ℃) has fine grains of polygonal ferrite.Large amounts of nanometer TiC particles exist in the tested steel at 600 ℃ for 1 h of insulation with significant precipitation strengthening,while the precipitation of TiC particles in the steel sample without insulation is inhibited with obvious decrease of precipitation strengthening effectiveness.

参考文献

[1] 霍向东,毛新平,李烈军,林振源.薄板坯连铸连轧生产Ti微合金化钢的强化机理[J].钢铁,2007(10):64-67.
[2] 周平,兰亮云,邱春林,霍孝新,高秀华,刘相华.X100管线钢的热轧显微组织分析[J].钢铁,2010(09):77-81.
[3] 刘东升,邹志文,岳重祥.采用控轧控冷技术(TMCP)生产合金减量型高强度船板[J].金属热处理,2012(02):57-64.
[4] 霍向东,毛新平,杨青峰,柴毅忠,陈康敏.CSP热轧工艺对Ti微合金化钢组织和性能的影响[J].钢铁钒钛,2010(02):26-31.
[5] Ooi S W;Fourlaris G A.Comparative study of precipitation effects in Ti only and Ti-V ultra low carbon (ULC) strip steels[J].Materials Characterization,2006(56):214-220.
[6] 谢利群,毛新平,霍向东.Ti对钢的组织性能的影响[J].冶金丛刊,2005(01):1-4,8.
[7] Honeycombe R W K;Mehl Medlist R F .Transformation form austenite in alloy steels[J].Metallurgical Transactions,1976,7A(07):915-936.
[8] Gladman T;Dulieu D;Mcivor I D.Structure-property relationships in high-strength microalloyed steels[A].Union Carbide Corp,New York,1977:32-55.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%