研究了采用分步法制备MoS2/Ti3SiC2层状复合材料的工艺,其制备过程分2步进行.首先制备Ti3SiC2高纯粉,再在1 400℃,30 MPa条件下热压烧结制备MoS2/Ti3SiC2层状复合材料.其MoS2含量分别为2%,4%,6%,8%(w/%).用XRD分析比较4种不同MoS2含量的烧结试样的相组成,并测试维氏硬度和电导率.实验结果表明,当MoS2含量为4%时,MoS2/Ti3SiC2烧结试样的硬度达到7.83 GPa,且电导率达到10.05×106 S·m-1.MoS2含量再增加时,烧结试样的硬度有所增大,但电导率有所下降.
参考文献
| [1] | Jeitschko W;Nowotny H .[J].Monatasch Chem,1967,98:329. |
| [2] | 阮汝祥.钛碳化硅（Ti3SiC2）--一种新的高温材料[J].材料工程,1997(05):99998. |
| [3] | Barsoum M W .The MN+1AXN Phases:Anew Class of Solids;Thermodynamically Stable Nan laminates[J].Progress in Solid State Chemistry,2000,28:201-281. |
| [4] | Barsoum MW.;Elraghy T. .SYNTHESIS AND CHARACTERIZATION OF A REMARKABLE CERAMIC - TI3SIC2[J].Journal of the American Ceramic Society,1996(7):1953-1956. |
| [5] | Barsoum MW.;Ogbuji LUJT.;Elraghy T. .OXIDATION OF TI3SIC2 IN AIR[J].Journal of the Electrochemical Society,1997(7):2508-2516. |
| [6] | Barsoum, M.W.;El-Raghy, T.;Rawn, C.J.;Porter, W.D.;Wang, H.;Payzant, E.A.;Hubbard, C.R. .Thermal properties of Ti_3SiC_2[J].The journal of physics and chemistry of solids,1999(4):429-439. |
| [7] | 陈福,方万标,赵恩录,张文玲,苟金芳,曾雄伟.高性能陶瓷材料Ti3SiC2 的研究进展[J].陶瓷,2006(12):19-22. |
| [8] | 陈艳林,梅炳初,朱教群.可加工陶瓷Ti3SiC2的合成和性能[J].硅酸盐通报,2003(03):74-77,96. |
| [9] | 范强,刘炎军,尹洪峰.层状陶瓷Ti3SiC2的研究现状[J].耐火材料,2003(01):56-59. |
| [10] | 朱教群,梅炳初,陈艳林.层状三元碳化物Ti3SiC2及其制备研究[J].武汉理工大学学报,2002(05):36-39. |
| [11] | 李世波,成来飞,王东,张立同.层状Ti3SiC2陶瓷的组织结构及力学性能[J].复合材料学报,2002(06):20-24. |
| [12] | 刘俊,梅炳初,朱教群,徐学文.Ti3SiC2陶瓷的制备及性能研究[J].江苏陶瓷,2003(03):9-11. |
| [13] | 陈艳林,朱教群,梅炳初.一种非同寻常的陶瓷-Ti3SiC2 陶瓷[J].佛山陶瓷,2001(07):1-4. |
| [14] | 陈艳林,梅炳初,朱教群.用热压法制备Ti3SiC2层状陶瓷的研究[J].陶瓷学报,2004(01):55-59. |
| [15] | 昝青峰,汪长安,黄勇,李翠伟,赵世柯.Al2O3/Ti3SiC2层状复合材料的制备与性能[J].材料工程,2003(09):15-17,21. |
| [16] | 天津市工业展览馆MoS2编写组.新型固体润滑材料MoS2[M].天津:天津人民出版社,1971:1-3. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%