本文采用水基凝胶注模成型工艺,通过控制技术参数,制备了固相含量为62%,粘度达到280mpa·s的钛酸铝陶瓷浆料.研究了抽真空时间对致密度以及固化时间的影响.随着有机单体和交联剂含量的增加,坯体的弯曲强度逐渐增大.通过分析影响因素,并改善制备条件,能够制备出强度为33.4MPa、可进行机加工的陶瓷坯体.
参考文献
| [1] | 方青,张联盟,沈强,李明忠.钛酸铝陶瓷及其研究进展[J].硅酸盐通报,2003(01):49-53. |
| [2] | Janney M A;Omateta O O .Method for Molding Ceramic Powders Using a Waterbased Gelcasting Process[P].US 5145908,1992-7-2. |
| [3] | Janney M A .Method for Molding Ceramic Powder[P].US 4894194,1990-1-16. |
| [4] | Omateta O O;Pollinger J P.Gelcasting and Aqueous Injection Molding for Silicon Nitride Structural Ceramic[A].USA:Materials Research Laboratory at UCSB,1997:25-31. |
| [5] | 刘宜勇;苏文强;钱瑞芬 .[J].陶瓷工程,1993,33(01):52-55. |
| [6] | Rolf Wasche .Gabriele Steinborn[J].Key Engineering Materials,1997,132－136:374-377. |
| [7] | Mak A Janney .[J].American Ceramic Society,1998,81(03):581-583. |
| [8] | P Sequlveda .[J].American Ceramic Society of Bulletin,1997,76(10):61-65. |
| [9] | G Sarbajit;E N Abbas .[J].American Ceramic Society,1999,82(03):513-520. |
| [10] | 芦令超,申玉芳,常钧,刘福田,程新,郭建亭.氧化铝陶瓷料浆流变性的研究[J].硅酸盐通报,2003(04):36-40. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%