针对高C3S熟料矿物体系,研究了BaO对相应的高钙生料易烧性的影响,并通过XRD、SEM研究了熟料矿物的结晶状况.结果表明:在较低烧成温度下(≤1350℃),掺入适量BaO后,能较明显地改善生料的易烧性,对矿物结晶影响不明显;但是在较高烧成温度下(>1350℃),掺入BaO对改善生料的易烧性不利,C3S结晶程度下降,晶体尺寸均匀性降低.另外还对BaO影响高钙生料易烧性的机制进行了探讨.
参考文献
[1] | A Kumllick;S R Bhargawa.Use of fluorspar and barite for improved burnability and clinkerisation of cement raw mixes[A].Cothenburg,Sedwen,1997:11031. |
[2] | J I Bhatty.Role of minor element in cement manufacture and use[M].Portland Cement Association,Skokie,IL,USA,1995 |
[3] | G K Moir;F P Glasser.Mineralisers,modifiers and activators in the clinkering process[A].New Delhi,1992:125-152. |
[4] | 张文生,欧阳世翕,陈益民.CaO-Al2O3-BaSO4系统物相形成及其动力学初探[J].硅酸盐学报,2001(04):305-308. |
[5] | 王政,张玉珍.BaSO4对C2S结构及性能的影响[J].硅酸盐学报,2001(02):196-198. |
[6] | N K Katyal;S C Ahluwalia;R Parkash .Effect of barium on the formation of tricalcium silicate[J].Cement and Concrete Research,1999,29:1857-1862. |
[7] | 马先伟,陈胡星.掺杂对高钙生料易烧性的影响[J].材料科学与工程学报,2003(06):872-874. |
[8] | W Kurdowsk;R Wollat .Solid solution of BaO in tricalcium silicate[J].Silicates Industries,1970,35:153-159. |
[9] | P Appendino;M Montorsi .The influence of Sr,Ba and Mg on the polymorphous transformations of tricalcium silicate[J].Ⅱ Cement,1971,68(03):89-98. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%