采用快速退火工艺在Pt/Ti/SiO2/p-Si衬底上制备了Bi4Ti3O12铁电薄膜.研究了退火温度对薄膜微观结构、铁电特性及介电性能的影响.研究表明:退火温度对Si基Bi4Ti3O12铁电薄膜晶相结构的影响显著,对晶粒尺寸和表面形貌的影响较小,但退火温度超过800℃后会出现焦绿石等杂相;低于750℃时,薄膜的剩余极化随退火温度升高而增大,高于750℃时却有所减小,但矫顽电场随退火温度升高而逐渐降低;退火温度对薄膜的漏电流密度有一定的影响,薄膜的漏电流密度在200kV/cm极化电场作用下低于3×10-9A/cm2,750℃时的剩余极化和矫顽电场分别为11μC/cm2和77kV/cm,具有较好的铁电和介电性能.
参考文献
| [1] | Woo-Chul Yi;Chang-Su Seo;Sook-II Kwun .Temperature dependence of capacitance/current-voltage characteristics of highly (0001)-oriented YMnO_(3) thin films on Si[J].Applied physics letters,2000(7):1044-1046. |
| [2] | Scott J F .[J].Ferroelectrics,2000,241:247-258. |
| [3] | Jun Yu;Hua Wang;Bairu Zhao et al.[J].Jpn J Appl Phys,2004,43(5A):2435-2437. |
| [4] | Akira Shibuya;Minoru Noda;Masanori Okuyama .[J].Japanese Journal of Appl Phys,2003,42(9B):5986-5989. |
| [5] | T.Watanabe;K.Saito;H.Funakubo .[J].Journal of Crystal Growth,2002,235:289-393. |
| [6] | Masashi Tanaka;Tohru Higuchi;Kazuhide Kudoh;Takeyo Tsukamoto .[J].Japanese Journal of Appl Phys,2002,41(3A):1536-1537. |
| [7] | Qunbao Yang;Yongxiang Li;Qingrui Yin et al.[J].Journal of the European Ceramic Society,2003,23:161-166. |
| [8] | D.Rugar;P.Hansma .[J].Physics Today,1990,43(10):23-30. |
| [9] | K.Ntu;J.W.Mayer;L.C.Feldman.Electric Thin Film Sciences:For Electrical Engineers & Material Scientists[M].Macmilan College Publishing Company,Inc,1992 |
| [10] | N.Maffei;S.B.Krupanidhi .[J].J Appl Phys,1992,72(08):3617-3621. |
| [11] | 顾豪爽 .溶胶凝胶制备Bi4Ti3O12铁电薄膜及其性能研究[D].武汉:华中理工大学,1996. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%